Synthesis of nanocrystalline LaF3 doped silica glasses by hydrofluoric acid catalyzed sol-gel process

Silica glasses doped with LaF3 nanocrystals were prepared by HF-catalyzed sol-gel method. HF was used both as fluorine source and as catalyst of the sol-gel reaction, making it possible to shorten the processing time with reducing the concentration of SiOH groups to similar to 10(18) cm(-3). The resultant glasses are transparent at visible spectral range, and the optical loss at the ultraviolet absorption edge is dominated by the Rayleigh scattering from LaF3 crystallites. The size of LaF3 crystallites increases with an increase in the sintering temperature and time, and is smaller than similar to 40 nm in samples showing good visible transparency. Green upconversion photoluminescence is observed in an Er3+-doped sample under excitation at 980 nm. (c) 2012 Elsevier B.V. All rights reserved.