Preparation and characterization of a porous silicate material from silica fume

被引:9
作者
Zhang, Yinmin [1 ]
Qi, Haiping [1 ]
Li, Yaqiong [1 ]
Zhang, Yongfeng [1 ]
Sun, Junmin [1 ]
机构
[1] Inner Mongolia Univ Technol, Coll Chem Engn, Hohhot 010051, Peoples R China
关键词
Silica Fume; Porous Silicate Material; Preparation; Mesoporous Material; MECHANICAL-PROPERTIES; ADSORPTION; CONCRETE; DESORPTION;
D O I
10.1007/s11814-017-0228-5
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
A porous silicate material derived from silica fume was successfully prepared and characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier-transform infrared (FT-IR) spectroscopy, Thermogravimetry and Differential thermal gravity (TG-DTG), N-2 adsorption and desorption isotherms, and scanning electron microscopy (SEM). Raw silica fume was analyzed by XRD, FT-IR and SEM. The analysis results of silica fume indicated that SiO2 in silica fume is mainly determined as amorphous state, and that the particles of raw silica fume exhibited characteristic spherical structure with a diameter of from 50 nm to 200 nm. The preparation of the porous silicate material involved two steps. The first step was the extraction of the SiO (3) (2-) leachate from raw silica fume. The maximum value of SiO (3) (2-) extraction yield was obtained under the following conditions: reaction temperature of 120 A degrees C, reaction time of 120 min, NaOH concentration of 15%, and alkali to SiO2 molar ratio of 2. The second step was the preparation of the porous silicate material though the reaction of SiO (3) (2-) leachate and Ca(OH)(2) suspension liquid. The optimum preparation conditions were as follows: preparation temperature of 90 A degrees C, preparation time of 1.5 h, Si/Ca molar ratio of 1 : 1, and stirring rate of 100 r/min. The BET surface area and pore size of the porous silicate material were 220.7 m(2)center dot g(-1) and 8.55 cm(3)/g, respectively. The porous silicate material presented an amorphous and unordered structure. The spectroscopic results indicated that the porous silicate material was mainly composed of Si, Ca, O, C, and Na, in the form of Ca2+, SiO (3) (2-) , CO (3) (2-) and Na+ ions, respectively, which agreed with the XRD, TG-DSC, and FT-IR data. The N-2 adsorption-desorption isotherm mode indicates that the porous silicate material belonged to a typical mesoporous material. The porous silicate material presented efficiency for the removal of formaldehyde: it showed a formaldehyde adsorption capacity of 8.01 mg/g for 140 min at 25 A degrees C.
引用
收藏
页码:3185 / 3194
页数:10
相关论文
共 50 条
[31]   Hydration Characteristics and Hydration Products of Tricalcium Silicate Doped with Superplasticizer and Silica Fume [J].
Ding, Qingjun ;
Wang, Yu ;
Huang, Xiulin .
FUNDAMENTAL OF CHEMICAL ENGINEERING, PTS 1-3, 2011, 233-235 :2589-2594
[32]   Recovery of silicon from silica fume [J].
Barati, M. ;
Sarder, S. ;
McLean, A. ;
Roy, R. .
JOURNAL OF NON-CRYSTALLINE SOLIDS, 2011, 357 (01) :18-23
[33]   Polymer cement mortar strengthened RC beams with/without silica fume as repair material [J].
Mizan, Mahmudul Hasan ;
Matsumoto, Koji .
CONSTRUCTION AND BUILDING MATERIALS, 2023, 409
[34]   Impact of Silica Fume on Fly Ash Based Concrete Material [J].
Sahoo, A. K. ;
Kar, B. B. .
ASIAN JOURNAL OF WATER ENVIRONMENT AND POLLUTION, 2022, 19 (04) :49-54
[35]   Fractual characterization of porous materials from layered silicate mineral [J].
Yang, Huaming ;
Zhang, Hua ;
Tang, Aidong .
2011 AASRI CONFERENCE ON INFORMATION TECHNOLOGY AND ECONOMIC DEVELOPMENT (AASRI-ITED 2011), VOL 3, 2011, :318-321
[36]   Optimizing cement-based material formulation for 3D printing: Integrating carbon nanotubes and silica fume [J].
Nassrullah, Ghaith ;
Ali, Mohd Mukarram ;
Al-Rub, Rashid K. Abu ;
Cho, Chung-Suk ;
El-Khasawneh, Bashar ;
Ghaffar, Seyed Hamidreza ;
Kim, Tae-Yeon .
CASE STUDIES IN CONSTRUCTION MATERIALS, 2025, 22
[37]   Fractual characterization of porous materials from layered silicate mineral [J].
Yang, Huaming ;
Zhang, Hua ;
Tang, Aidong .
2011 INTERNATIONAL CONFERENCE ON FUZZY SYSTEMS AND NEURAL COMPUTING (FSNC 2011), VOL VI, 2011, :541-544
[38]   In-situ formation of geopolymer foams through addition of silica fume: Preparation and sinterability [J].
Sawan, S. E. Abo ;
Zawrah, M. F. ;
Khattab, R. M. ;
Abdel-Shafi, Ayman A. .
MATERIALS CHEMISTRY AND PHYSICS, 2020, 239
[39]   Rapid synthesis of morphology-controlled mesoporous silica nanoparticles from silica fume [J].
Zhou, Chunyu ;
Yan, Chunjie ;
Zhao, Junjie ;
Wang, Hongquan ;
Zhou, Qi ;
Luo, Wenjun .
JOURNAL OF THE TAIWAN INSTITUTE OF CHEMICAL ENGINEERS, 2016, 62 :307-312
[40]   Functionalized silica fume for chromium (VI) removal from wasterwater [J].
Zhou, Yang ;
Wang, Shixing ;
Xie, Keqiang ;
Dai, Yongnian ;
Ma, Wenhui .
ADVANCED MATERIAL SCIENCE AND TECHNOLOGY, PTS 1 AND 2, 2011, 675-677 :93-+