Preparation and characterization of a porous silicate material from silica fume

被引:9
|
作者
Zhang, Yinmin [1 ]
Qi, Haiping [1 ]
Li, Yaqiong [1 ]
Zhang, Yongfeng [1 ]
Sun, Junmin [1 ]
机构
[1] Inner Mongolia Univ Technol, Coll Chem Engn, Hohhot 010051, Peoples R China
关键词
Silica Fume; Porous Silicate Material; Preparation; Mesoporous Material; MECHANICAL-PROPERTIES; ADSORPTION; CONCRETE; DESORPTION;
D O I
10.1007/s11814-017-0228-5
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
A porous silicate material derived from silica fume was successfully prepared and characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier-transform infrared (FT-IR) spectroscopy, Thermogravimetry and Differential thermal gravity (TG-DTG), N-2 adsorption and desorption isotherms, and scanning electron microscopy (SEM). Raw silica fume was analyzed by XRD, FT-IR and SEM. The analysis results of silica fume indicated that SiO2 in silica fume is mainly determined as amorphous state, and that the particles of raw silica fume exhibited characteristic spherical structure with a diameter of from 50 nm to 200 nm. The preparation of the porous silicate material involved two steps. The first step was the extraction of the SiO (3) (2-) leachate from raw silica fume. The maximum value of SiO (3) (2-) extraction yield was obtained under the following conditions: reaction temperature of 120 A degrees C, reaction time of 120 min, NaOH concentration of 15%, and alkali to SiO2 molar ratio of 2. The second step was the preparation of the porous silicate material though the reaction of SiO (3) (2-) leachate and Ca(OH)(2) suspension liquid. The optimum preparation conditions were as follows: preparation temperature of 90 A degrees C, preparation time of 1.5 h, Si/Ca molar ratio of 1 : 1, and stirring rate of 100 r/min. The BET surface area and pore size of the porous silicate material were 220.7 m(2)center dot g(-1) and 8.55 cm(3)/g, respectively. The porous silicate material presented an amorphous and unordered structure. The spectroscopic results indicated that the porous silicate material was mainly composed of Si, Ca, O, C, and Na, in the form of Ca2+, SiO (3) (2-) , CO (3) (2-) and Na+ ions, respectively, which agreed with the XRD, TG-DSC, and FT-IR data. The N-2 adsorption-desorption isotherm mode indicates that the porous silicate material belonged to a typical mesoporous material. The porous silicate material presented efficiency for the removal of formaldehyde: it showed a formaldehyde adsorption capacity of 8.01 mg/g for 140 min at 25 A degrees C.
引用
收藏
页码:3185 / 3194
页数:10
相关论文
共 50 条
  • [1] Preparation and characterization of a porous silicate material from silica fume
    Yinmin Zhang
    Haiping Qi
    Yaqiong Li
    Yongfeng Zhang
    Junmin Sun
    Korean Journal of Chemical Engineering, 2017, 34 : 3185 - 3194
  • [2] Preparation and characterization of a novel porous silicate material from coal gangue
    Gao, Yajun
    Huang, Huijuan
    Tang, Wenjing
    Liu, Xiaoyao
    Yang, Xinyu
    Zhang, Jianbin
    MICROPOROUS AND MESOPOROUS MATERIALS, 2015, 217 : 210 - 218
  • [3] Preparation of porous consolidated zeolite from silica fume and characteristics of humidity conditioning
    Miyazaki M.
    Nishikawa Y.
    Shiomi H.
    Shiono T.
    Zairyo/Journal of the Society of Materials Science, Japan, 2020, 69 (07) : 522 - 526
  • [4] Preparation of porous and nonporous silica nanofilms from aqueous sodium silicate
    He, JH
    Fujikawa, S
    Kunitake, T
    Nakao, A
    CHEMISTRY OF MATERIALS, 2003, 15 (17) : 3308 - 3313
  • [5] Sustainable route for silica preparation from silica fume
    Deng, Jiabao
    Luo, Dawei
    Rong, Ke
    ENVIRONMENTAL TECHNOLOGY, 2024,
  • [6] A New Porous Hybrid Material Derived From Silica Fume and Alginate for Sustainable Pollutants Reduction
    Zanoletti, Alessandra
    Vassura, Ivano
    Venturini, Elisa
    Monai, Matteo
    Montini, Tiziano
    Federici, Stefania
    Zacco, Annalisa
    Treccani, Laura
    Bontempi, Elza
    FRONTIERS IN CHEMISTRY, 2018, 6
  • [7] Silica Fume Slurry Lagoon Closure: Thixotropic Material Characterization and Solidification
    Grubb, Dennis G.
    Berggren, Dusty R. V.
    Toburen, Charles S.
    Powers, Martin T.
    JOURNAL OF HAZARDOUS TOXIC AND RADIOACTIVE WASTE, 2025, 29 (01)
  • [8] Characterization of Magnesium Silicate Hydrate (MSH) Gel Formed by Reacting MgO and Silica Fume
    Zhang, Tingting
    Zou, Jing
    Wang, Baomin
    Wu, Zhenlin
    Jia, Yuan
    Cheeseman, Christopher R.
    MATERIALS, 2018, 11 (06):
  • [9] Preparation and characterization of a porous silicate material using a CO2-storage material for CO2 adsorption
    Liu, Xiaoyao
    Yang, Xinyu
    Du, Hong
    Wu, Yu
    Zhang, Xuesen
    Zhang, Jianbin
    POWDER TECHNOLOGY, 2018, 333 : 138 - 152
  • [10] Preparation and Characterization of Hierarchically Porous Silica Monoliths
    Guo Xing-Zhong
    Shan Jia-Qi
    Ding Li
    Yu Huan
    Zhang Xiao-Qi
    Yang Hui
    CHINESE JOURNAL OF INORGANIC CHEMISTRY, 2015, 31 (04) : 635 - 640