A study on mechanism of corrosion protection of polyaniline coating and its failure

被引：141

作者：

Fang, Jianjun ^{[1
]}

Xu, Ke ^{[1
]}

Zhu, Lihua ^{[1
]}

Zhou, Zhixiong ^{[1
]}

Tang, Heqing ^{[1
]}

机构：

[1] Huazhong Univ Sci & Technol, Dept Chem & Chem Engn, Wuhan 430074, Peoples R China

来源：

CORROSION SCIENCE | 2007年 / 49卷 / 11期

关键词：

polyaniline; stainless steel; corrosion; electrodeposited films; galvanic coupling;

D O I：

10.1016/j.corsci.2007.05.017

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Polyaniline (PANI) coatings were electrochemically deposited on substrates of stainless steel and platinum in solutions of 0.2 M H2SO4 and 0.1 M aniline by cyclic voltammetry. The corrosion protection of the PANI coatings and their failure were investigated in 0.2 M H2SO4 solution. It was observed that the corrosion protection ability of the coating to steel substrate was increased with the increase of the coating thickness. The corrosion protection ability was mainly attributed to the passivating effect of PANI due to its oxidizing ability in its emeraldine state. During its operation, the PANI coating in emeraldine state tended to gradually lose its corrosion protection ability. This gradual failure of the PANI coating, but faster than expected, was confirmed to be related to a gradual reduction of the emeraldine PANI and a gradually increased resistance between the PANI coating and the stainless steel substrate. These findings lead to a new mechanism for the corrosion protection of PANI coating and its failure. (c) 2007 Elsevier Ltd. All rights reserved.

引用

页码：4232 / 4242

页数：11

共 50 条

[31] Preparation of polyaniline-TiO2 composite and its comparative corrosion protection performance with polyaniline
Sathiyanarayanan, S.
Azim, S. Syed
Venkatachari, G.
SYNTHETIC METALS, 2007, 157 (4-5) : 205 - 213
[32] A ternary MWCNT/Ceria/Polyaniline composite for corrosion protection
Oueiny, C.
Berlioz, S.
Perrin, F. X.
20TH INTERNATIONAL CONFERENCE ON COMPOSITE MATERIALS, 2015,
[33] Electrochemical deposition and characterization of polyaniline-graphene nanocomposite films and its corrosion protection properties
Jafari, Yaser
Ghoreishi, Sayed Mehdi
Shabani-Nooshabadi, Mehdi
JOURNAL OF POLYMER RESEARCH, 2016, 23 (05)
[34] Corrosion protection of stainless steel by polyaniline electrosynthesized from phosphate buffer solutions
Moraes, SR
Huerta-Vilca, D
Motheo, AJ
PROGRESS IN ORGANIC COATINGS, 2003, 48 (01) : 28 - 33
[35] Corrosion protection by polyaniline-coated latex microspheres
Abu, YM
Aoki, K
JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2005, 583 (01) : 133 - 139
[36] The electrochemical synthesis of polyaniline on stainless steel and its corrosion performance
Özyilmaz, AT
Erbil, M
Yazici, B
CURRENT APPLIED PHYSICS, 2006, 6 (01) : 1 - 9
[37] Graphene coating for anti-corrosion and the investigation of failure mechanism
Zhu, Y. X.
Duan, C. Y.
Liu, H. Y.
Chen, Y. F.
Wang, Y.
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2017, 50 (11)
[38] Developing of Polyaniline Coating on Rotating Steel Cylinder for Improving Its Corrosion Resistance
El-Shazly, A. H.
Al-Turaif, H. A.
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2012, 7 (06): : 5388 - 5399
[39] Electrodeposition of Ni(OH)2 reinforced polyaniline coating for corrosion protection of 304 stainless steel
Jiang, Li
Syed, Junaid Ali
Gao, Yangzhi
Lu, Hongbin
Meng, Xiangkang
APPLIED SURFACE SCIENCE, 2018, 440 : 1011 - 1021
[40] Active corrosion protection of epoxy coating filled with surface-engineered cellulose nanocrystals with polyaniline
Shahnavaz, Alireza
Shojaei, Akbar
Rahmani, Pooria
Ahadian, Mohammad Mahdi
INTERNATIONAL JOURNAL OF BIOLOGICAL MACROMOLECULES, 2025, 302

← 1 2 3 4 5 →