Microwave-hydrothermal synthesis of mesoporous γ-Al2O3 and its impregnation with AgNPs for excellent catalytic oxidation of CO

被引：0

作者：

Kundu, Sukanya ^{[1
]}

Naskar, Milan Kanti ^{[1
]}

机构：

[1] CSIR Cent Glass & Ceram Res Inst, Sol Gel Div, Kolkata 700032, India

来源：

BULLETIN OF MATERIALS SCIENCE | 2018年 / 41卷 / 06期

关键词：

Microwave hydrothermal; microstructure; mesoporous Al2O3; CO oxidation; CARBON-MONOXIDE; GAMMA-ALUMINA; METAL; PHOTODEGRADATION; EXPOSURE;

D O I：

10.1007/s12034-018-1675-2

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Mesoporous.-alumina was synthesized by the microwave-hydrothermal process with a shorter duration time at 150. C/2 h followed by calcination at 550. C/1 h. Ag nanoparticles (AgNPs) were impregnated into.-alumina under a reducing atmosphere at 450. C. The synthesized product was characterized by X-ray diffraction (XRD), thermogravimetric (TG)/differential thermal analysis (DTA), X-ray photoelectron spectroscopy (XPS), N2 adsorption-desorption study, fieldemission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). The BET surface area values of.-alumina and Ag-impregnated.-alumina were found to be 258 and 230 m2 g-1, respectively. FESEM images showed the formation of grain-like particles of 50-70 nm in size with a flake-like microstructure. The XRD, XPS and TEM studies confirmed the presence of Ag in the synthesized product. Catalytic properties of the product for CO oxidation was studied with the T50 (50% conversion) and T100 (100% conversion) values of 118 and 135. C, respectively; the enhanced values were compared with the literature reported values.

引用

页数：8

共 35 条

[11] EFFECTS ON EXPERIMENTAL ANIMALS OF LONG-TERM INHALATION EXPOSURE TO CARBON MONOXIDE [J].

JONES, RA ;

STRICKLAND, JA ;

STUNKARD, JA ;

SIEGEL, J .

TOXICOLOGY AND APPLIED PHARMACOLOGY, 1971, 19 (01) :46-+

[12] CO oxidation on a copper-modified Pt(111) surface [J].

Kolodziejczyk, M ;

Colen, RER ;

Berdau, M ;

Delmon, B ;

Block, JH .

SURFACE SCIENCE, 1997, 375 (2-3) :235-249

[13] Unsupported nanoporous Ag catalysts towards CO oxidation [J].

Kou, Tianyi ;

Li, Dongwei ;

Zhang, Chi ;

Zhang, Zhonghua ;

Yang, Hua .

JOURNAL OF MOLECULAR CATALYSIS A-CHEMICAL, 2014, 382 :55-63

[14] Self-Assembled 3D Hierarchically Structured Gamma Alumina by Hydrothermal Method [J].

Li, Yanhui ;

Peng, Cheng ;

Li, Lianglong ;

Rao, Pinggen .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2014, 97 (01) :35-39

[15] A facile route to ordered mesoporous-alumina-supported catalysts, and their catalytic activities for CO oxidation [J].

Li, Zhen-Xing ;

Shi, Fu-Bo ;

Li, Le-Le ;

Zhang, Tao ;

Yan, Chun-Hua .

PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 2011, 13 (07) :2488-2491

[16] Ordered crystalline alumina molecular sieves synthesized via a nanocasting route [J].

Liu, Qian ;

Wang, Aiqin ;

Wang, Xiaodong ;

Zhang, Tao .

CHEMISTRY OF MATERIALS, 2006, 18 (22) :5153-5155

[17] Effect of anions during hydrothermal preparation of boehmites [J].

Mishra, D ;

Anand, S ;

Panda, RK ;

Das, RP .

MATERIALS LETTERS, 2002, 53 (03) :133-137

[18] Hydrothermal Synthesis of Petal-Like Alumina Flakes [J].

Naskar, Milan Kanti .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2009, 92 (10) :2392-2395

[19] Preparation of Nano Alumina Powder via Combustion Synthesis: Porous Structure Optimization via Taguchi L16 Design [J].

Norouzbeigi, Reza ;

Edrissi, Mohammad .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2011, 94 (11) :4052-4058

[20] Evaluation of a spinel based pigment system as a CO oxidation catalyst [J].

PalDey, S ;

Gedevanishvili, S ;

Zhang, W ;

Rasouli, F .

APPLIED CATALYSIS B-ENVIRONMENTAL, 2005, 56 (03) :241-250

← 1 2 3 4 →