Brazing of 6061 aluminum alloy/Ti-6Al-4V using Al-Si-Cu-Ge filler metals

被引：73

作者：

Chang, S. Y. ^{[1
]}

Tsao, L. C. ^{[2
]}

Lei, Y. H. ^{[1
]}

Mao, S. M. ^{[1
]}

Huang, C. H. ^{[3
]}

机构：

[1] Natl Yunlin Univ Sci & Technol, Dept Mech Engn, Touliu 64002, Yunlin, Taiwan

[2] Natl Pingtung Univ Sci & Technol, Dept Mat Engn, Neipu 91201, Pingtung, Taiwan

[3] Met Ind Res & Dev Ctr, Kaohsiung 81160, Taiwan

来源：

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY | 2012年 / 212卷 / 01期

关键词：

Brazing; Aluminum alloys; Ti-6Al-4V; Al-Si-Cu-Ge alloys; Rare-earth elements; MICROSTRUCTURE;

D O I：

10.1016/j.jmatprotec.2011.07.014

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Al-8.4Si-20Cu-10Ge and mixed rare-earth elements (Re) containing Al-8.4Si-20Cu-10Ge-0.1Re filler metals were used for brazing of 6061 aluminum alloy/Ti-6Al-4V. The addition of 20 wt.% copper and 10 wt.% germanium into the Al-12Si filler metal lowered the solidus temperature from 586 degrees C to 489 degrees C and the liquidus temperature from 592 degrees C to 513 degrees C. The addition of 0.1 wt.% rare-earth elements into Al-8.4Si-20Cu-10Ge alloy caused remarkable Al-rich phase refinement and transformed the needle-like Al2Cu intermetallic compounds into block-like shapes. Shear strengths of the 6061 aluminum alloy/Ti-6AI-4V joints with the two brazing filler metals. Al-8.4Si-20Cu-10Ge and Al-8.4S-20Cu-10Ge-0.1Re, varied insignificantly with brazing periods of 10-60 min. The average shear strength of the 6061 aluminum alloy/Ti-6Al-4V joints brazed with Al-8.4Si-20Cu-10Ge at 530 degrees C was about 20 MPa. Rare-earth elements appeared to improve the reaction of the Al-8.45i-20Cu-10Ge filler metal with Ti-6Al-4V. The joint shear strength of the 6061 aluminum alloy/TI-6Al-4V with Al-8.4Si-20Cu-10Ge-0.1 Re reached about 51 MPa. (C) 2011 Elsevier B.V. All rights reserved.

引用

页码：8 / 14

页数：7

共 8 条

[1] Joining 6061 aluminum alloy with Al-Si-Cu filler metals [J].

Chang, S. Y. ;

Tsao, L. C. ;

Li, T. Y. ;

Chuang, T. H. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 488 (01) :174-180

[2] Development of a low-melting-point filler metal for brazing aluminum alloys [J].

Chuang, TH ;

Yeh, MS ;

Tsao, LC ;

Tsai, TC ;

Wu, CS .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (09) :2239-2245

[3]

Jacobson DM, 1996, WELD J, V75, pS243

[4] Corrosion and mechanical-micro structural aspects of dissimilar joints of Ti-6Al-4V and Al plates [J].

Kahraman, Nizamettin ;

Gulenc, Behcet ;

Findik, Fehim .

INTERNATIONAL JOURNAL OF IMPACT ENGINEERING, 2007, 34 (08) :1423-1432

[5] Study on the Microstructure and Wettability of an Al-Cu-Si Braze Containing Small Amounts of Rare Earth Erbium [J].

Shi, Yaowu ;

Yu, Yang ;

Li, Yapeng ;

Xia, Zhidong ;

Lei, Yongping ;

Li, Xiaoyan ;

Guo, Fu .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2009, 18 (03) :278-281

[6] Microstructure and bonding mechanism of Al/Ti bonded joint using Al-10Si-1Mg filler metal [J].

Sohn, WH ;

Bong, HH ;

Hong, SH .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 355 (1-2) :231-240

[7] Brazeability of a 3003 aluminum alloy with Al-Si-Cu-based filler metals [J].

Tsao, LC ;

Weng, WP ;

Cheng, MD ;

Tsao, CW ;

Chuang, TH .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2002, 11 (04) :360-364

[8] The influence of rare earth elements on microstructures and properties of 6061 aluminum alloy vacuum-brazed joints [J].

Wang, SH ;

Zhou, HP ;

Kang, YP .

JOURNAL OF ALLOYS AND COMPOUNDS, 2003, 352 (1-2) :79-83

← 1 →