Fatigue Property in Ni-Based Bulk Metallic Glass

被引:2
作者
Fujita, Kazutaka [1 ]
Misumi, Kousuke [1 ]
Zhang, Wei [2 ]
Inoue, Akihisa
机构
[1] Ube Natl Coll Technol, Dept Mech Engn, Ube, Yamaguchi 7558555, Japan
[2] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan
关键词
fatigue; fatigue limit; bulk metallic glass; amorphous; fractography; FRACTURE-TOUGHNESS; STRENGTH; ALLOYS; AL;
D O I
10.2320/jinstmet.75.474
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Fatigue test was carried out on Ni-based bulk metallic glass (BMG) for which there is still no reports on fatigue strength. Test alloy rods with a diameter of 2 mm were prepared in Ni60Zr20Nb15Al5 at% systems by copper mold casting method. The tensile strength (sigma(B)) was 2.9 GPa. The test specimens were machined to hourglass shape type with a minimum diameter of 0.9 mm. The specimens were tested at a stress ratio of 0.1 and a frequency of 10 Hz. The fatigue limit (sigma(W)) and fatigue ratio (sigma(W)/sigma(B)) in the Ni-based BMG showed high values of 1.68 GPa and 0.58, respectively. The tendency that the sigma(W) increased with increasing the sigma(B) in BMGs was indicated in the Ni-based BMG. In addition, the fatigue fracture toughness in the Ni-based BMG showed a high value of 14 MPa.m(1/2).
引用
收藏
页码:474 / 478
页数:5
相关论文
共 50 条
  • [11] Micro-scale Compression of Ni-based Metallic Glass
    Wu, Bin
    Feng, Tao
    Rauf, Abdur
    Guo, Chun-Yu
    PROCEEDINGS OF THE 3RD ANNUAL INTERNATIONAL CONFERENCE ON ADVANCED MATERIAL ENGINEERING (AME 2017), 2017, 110 : 203 - 207
  • [12] A Highly Fatigue-Resistant Zr-Based Bulk Metallic Glass
    Steven E. Naleway
    Rawley B. Greene
    Bernd Gludovatz
    Neil K. N. Dave
    Robert O. Ritchie
    Jamie J. Kruzic
    Metallurgical and Materials Transactions A, 2013, 44 : 5688 - 5693
  • [13] Fatigue coaxing experiments on a Zr-based bulk-metallic glass
    El-Shabasy, Adel B.
    Lewandowski, John J.
    SCRIPTA MATERIALIA, 2010, 62 (07) : 481 - 484
  • [14] Pitting resistivity of Ni-based bulk metallic glasses in chloride solution
    Emran, Khadijah M.
    AL-Refai, Hanaa
    RSC ADVANCES, 2017, 7 (59): : 37349 - 37358
  • [15] Fatigue crack propagation behavior and fracture toughness in a Ni-free ZrCuFeAlikg bulk metallic glass
    Liu, Yan
    Wang, Yi-Mei
    Liu, Lin
    ACTA MATERIALIA, 2015, 92 : 209 - 219
  • [16] Enhancement of plasticity of Fe-based bulk metallic glass by Ni substitution for Fe
    Guo, S. F.
    Li, N.
    Zhang, C.
    Liu, L.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 504 : S78 - S81
  • [17] Fatigue strength in nanocrystalline Ti- and Cu-based bulk metallic glasses
    Fujita, Kazutaka
    Hashimoto, Tetsuro
    Zhang, Wei
    Nishiyama, Nobuyuki
    Ma, Chaoli
    Kimura, Hisamichi
    Inoue, Akihisa
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2006, 70 (10) : 816 - 823
  • [18] Fracture toughness in Zr-based bulk metallic glass
    Fujita, K
    Nishiyama, N
    Amiya, K
    Zhang, T
    Kimura, H
    Inoue, A
    Metastable, Mechanically Alloyed and Nanocrystalline Materials, 2005, 24-25 : 323 - 326
  • [19] Crystallization and thermal stability of Ni-based metallic glass with high tungsten and boron
    Yazici, Ziya Ozgur
    Hitit, Aytekin
    Sahin, Hakan
    Kara, Muhammet Emir
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2022, 590
  • [20] Fracture and fatigue behaviour of a laser additive manufactured Zr-based bulk metallic glass
    Best, James P.
    Ostergaard, Halsey E.
    Li, Bosong
    Stolpe, Moritz
    Yang, Fan
    Nomoto, Keita
    Hasib, M. Tarik
    Muransky, Ondrej
    Busch, Ralf
    Li, Xiaopeng
    Kruzic, Jamie J.
    ADDITIVE MANUFACTURING, 2020, 36 (36)