Fatigue Property in Ni-Based Bulk Metallic Glass

被引：2
|
作者：
Fujita, Kazutaka [1 ]
Misumi, Kousuke [1 ]
Zhang, Wei [2 ]
Inoue, Akihisa
机构：
[1] Ube Natl Coll Technol, Dept Mech Engn, Ube, Yamaguchi 7558555, Japan
[2] Tohoku Univ, Inst Mat Res, Sendai, Miyagi 9808577, Japan
来源：
JOURNAL OF THE JAPAN INSTITUTE OF METALS | 2011年 / 75卷 / 09期
关键词：
fatigue; fatigue limit; bulk metallic glass; amorphous; fractography; FRACTURE-TOUGHNESS; STRENGTH; ALLOYS; AL;
D O I：
10.2320/jinstmet.75.474
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Fatigue test was carried out on Ni-based bulk metallic glass (BMG) for which there is still no reports on fatigue strength. Test alloy rods with a diameter of 2 mm were prepared in Ni60Zr20Nb15Al5 at% systems by copper mold casting method. The tensile strength (sigma(B)) was 2.9 GPa. The test specimens were machined to hourglass shape type with a minimum diameter of 0.9 mm. The specimens were tested at a stress ratio of 0.1 and a frequency of 10 Hz. The fatigue limit (sigma(W)) and fatigue ratio (sigma(W)/sigma(B)) in the Ni-based BMG showed high values of 1.68 GPa and 0.58, respectively. The tendency that the sigma(W) increased with increasing the sigma(B) in BMGs was indicated in the Ni-based BMG. In addition, the fatigue fracture toughness in the Ni-based BMG showed a high value of 14 MPa.m(1/2).
引用
收藏
页码：474 / 478
页数：5
相关论文
共 50 条
  • [1] Effect of nanocrystalline dispersion on fatigue in a Zr-based bulk metallic glass
    Fujita, K
    Takayama, T
    Inoue, A
    Zhang, T
    Kimura, H
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2003, 67 (02) : 79 - 84
  • [2] Fatigue Properties and Morphology of Fatigue Fracture of Bulk Metallic Glass
    Zhao, X. Y.
    Chen, Z. H.
    Wang, H. P.
    Zhan, J.
    METAL SCIENCE AND HEAT TREATMENT, 2016, 58 (7-8) : 487 - 492
  • [3] Ductile Ni-based bulk metallic glasses at room temperature
    Zeng, Weiping
    Chen, Yanhua
    Li, Qiang
    Li, He
    Mu, Baoxia
    Ye, Jiankang
    Chang, Chuntao
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 26 : 2432 - 2442
  • [4] A novel Ni-based bulk metallic glass containing high amount of tungsten and boron
    Hitit, Aytekin
    Yazici, Ziya Ozgur
    Sahin, Hakan
    Ozturk, Pelin
    Asgin, Ahmet Malik
    Hitit, Burcu
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 807
  • [5] A Numerical Simulation of a Ni-based Bulk Metallic Glass During Compressive Deformation and Fracture
    Liang Weizhong
    Ning Zhiliang
    Liu Ailian
    An Yongliang
    MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2015, 18 : 20 - 23
  • [6] Glass forming ability and mechanical properties of new Ni-based bulk metallic glasses
    Li, Song
    Xie, Guoqiang
    Louzguine-Luzgin, Dmitri V.
    Inoue, Akihisa
    MATERIALS TRANSACTIONS, 2008, 49 (03) : 494 - 497
  • [7] Synthesis of Ni-based bulk metallic glasses for penetrating materials
    Shin, Jaehyuck
    Kwon, Jinwook
    Park, Joon Sik
    Bael, Donghyun
    MATERIALS TRANSACTIONS, 2008, 49 (08) : 1796 - 1799
  • [8] Optimization for toughness in metalloid-free Ni-based bulk metallic glasses
    Zhu, Zhen-dong
    Jia, Peng
    Xu, Jian
    SCRIPTA MATERIALIA, 2011, 64 (08) : 785 - 788
  • [9] Fatigue Properties and Morphology of Fatigue Fracture of Bulk Metallic Glass
    X. Y. Zhao
    Z. H. Chen
    H. P. Wang
    J. Zhan
    Metal Science and Heat Treatment, 2016, 58 : 487 - 492
  • [10] A Ni-free Zr-based bulk metallic glass with remarkable plasticity
    Jang, Jason S. C.
    Wu, K. C.
    Jian, S. R.
    Hsieh, P. J.
    Huang, J. C.
    Liu, C. T.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 : S109 - S114
12345