Pseudoelasticity in pseudo-binary Fe3(Al1-xGax) single crystals

被引:1
作者
Yasuda, H. Y. [1 ]
Shibata, K. [1 ]
Umakoshi, Y. [1 ]
机构
[1] Osaka Univ, Div Mat & Mfg Sci, Grad Sch Engn, Suita, Osaka 5650871, Japan
关键词
Iron aluminides (based on Fe3Al); Shape memory effects; Order/disorder transformations; Defects: dislocation geometry and arrangement; Electron microscopy; transmission; ORDERING PROCESS; FE3AL; ALLOYS;
D O I
10.1016/j.intermet.2011.07.028
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Pseudoelastic behavior of pseudo-binary Fe-3(Al1-xGax) single crystals with the D0(3) structure was examined focusing on the dependence on x and annealing condition. At x = 0.2-0.8, the D0(3) single phase developed below about 773-873 K. In the D0(3)-ordered crystals compressed with [(1) over bar 49] axis at room temperature, reversible motion of 1/4[111] superpartial dislocations dragging the antiphase boundaries (APB) contributed to the strain recovery, similar to Fe3Al and Fe3Ga binary crystals. In the pseudo-binary crystals after D0(3) ordering treatment by slow cooling, 1/4[111] superpartials trailing the nearest-neighbor APB were dominantly observed below x = 0.4 while the paired superpartials moved dragging the next-nearest-neighbor APB at and above x = 0.4. During unloading, both the APBs pulled back the superpartials due to their tension resulting in the pseudoelasticity. The amount of strain recovery varied with x, which was closely related to the dislocation configuration. Annealing in the D0(3) single-phase region affected the dislocation configuration and the backward stress due to APB, which influenced the pseudoelastic behavior. (C) 2011 Elsevier Ltd. All rights reserved.
引用
收藏
页码:1786 / 1793
页数:8
相关论文
共 17 条
[1]   On pseudoelasticity in single crystals of the intermetallic compound Fe3Al [J].
Brinck, A ;
Engelke, C ;
Neuhauser, H .
SCRIPTA MATERIALIA, 1997, 37 (05) :569-574
[2]   Phase equilibria and stability of ordered b.c.c. phases in the Fe-rich portion of the Fe-Ga system [J].
Ikeda, O ;
Kainuma, R ;
Ohnuma, I ;
Fukamichi, K ;
Ishida, K .
JOURNAL OF ALLOYS AND COMPOUNDS, 2002, 347 (1-2) :198-205
[3]   PSEUDOELASTICITY AND SLIP REVERSIBILITY IN DO3-ORDERED FE-AL SINGLE-CRYSTALS BY INSITU EXPERIMENTS [J].
KUBIN, LP ;
FOURDEUX, A ;
GUEDOU, JY ;
RIEU, J .
PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1982, 46 (03) :357-378
[4]   Pseudoelasticity in Fe3Al single crystals [J].
Langmaack, E ;
Nembach, E .
PHILOSOPHICAL MAGAZINE A-PHYSICS OF CONDENSED MATTER STRUCTURE DEFECTS AND MECHANICAL PROPERTIES, 1999, 79 (10) :2359-2377
[5]   PLASTIC DEFORMATION BEHAVIOUR OF LONG-RANGE ORDERED IRON-ALUMINIUM ALLOYS .I. SINGLE CRYSTAL DEFORMATION EXPERIMENTS [J].
LEAMY, HJ ;
KAYSER, FX ;
MARCINKOWSKI, MJ .
PHILOSOPHICAL MAGAZINE, 1969, 20 (166) :763-+
[6]   COMPRESSIVE DEFORMATION BEHAVIOR OF LONG RANGE ORDERED POLYCRYSTALLINE IRON-ALUMINUM ALLOYS [J].
LEAMY, HJ ;
KAYSER, FX .
PHYSICA STATUS SOLIDI, 1969, 34 (02) :765-&
[7]   DIRECT OBSERVATION OF ANTIPHASE BOUNDARIES IN FE3AL SUPERLATTICE [J].
MARCINKOWSKI, MJ ;
BROWN, N .
JOURNAL OF APPLIED PHYSICS, 1962, 33 (02) :537-&
[8]   THEORY AND DIRECT OBSERVATION OF DISLOCATIONS IN THE FE3AL SUPERLATTICES [J].
MARCINKOWSKI, MJ ;
BROWN, N .
ACTA METALLURGICA, 1961, 9 (08) :764-786
[9]  
NOSOVA GI, 1986, PHYS MET METALLOGR, V61, P151
[10]  
Otsuka K., 1998, Shape memory materials, P1