Surface globularization generated by standard PBF-EB Ti-6Al-4V processing achieves an improvement in fatigue performance

被引：4

作者：

Derimow, Nicholas ^{[1
]}

Hanson, Keenan ^{[2
]}

Moser, Newell ^{[1
]}

Kafka, Orion L. ^{[1
]}

Benzing, Jake T. ^{[1
]}

Hrabe, Nikolas ^{[1
]}

机构：

[1] NIST, Appl Chem & Mat Div, 325 Broadway, Boulder, CO 80305 USA

[2] Stryker, Mahwah, NJ 07430 USA

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2022年 / 159卷

关键词：

Additive manufacturing; Ti-6Al-4V; Powder recovery; Recrystallization; Fatigue; BEAM MELTING EBM; ELECTRON; DEFECTS; BEHAVIOR; ROUGHNESS; STRENGTH;

D O I：

10.1016/j.ijfatigue.2022.106810

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Standard electron beam powder-bed fusion Ti-6Al-4V powder recovery and hot-isostatic pressing has been found to result in a surface layer microstructure change to globular alpha/beta. Thickness control of this surface layer up to 15 mu m was demonstrated by varying powder recovery blasting working distance and duration. This surface globular layer was found to improve high-cycle rotating bending fatigue strength at 10(7) cycles by 60 MPa for specimens with smooth surfaces. The same trend was not observed for specimens with as-built surface roughness because globularization did not occur at dominant fatigue crack initiation sites; the roots of deep surface crevices.

引用

页数：13

共 30 条

[21]

Paraview.org, WELC PAR

[22] Fatigue performances of chemically etched thin struts built by selective electron beam melting: Experiments and predictions [J].

Persenot, Theo ;

Burr, Alexis ;

Dendievel, Remy ;

Buffiere, Jean-Yves ;

Maire, Eric ;

Lachambre, Joel ;

Martin, Guilhem .

MATERIALIA, 2020, 9

[23] Effect of ultrasonic shot peening on the surface defects of thin struts built by electron beam melting: Consequences on fatigue resistance [J].

Persenot, Theo ;

Burr, Alexis ;

Plancher, Emeric ;

Buffiere, Jean-Yves ;

Dendievel, Remy ;

Martin, Guilhem .

ADDITIVE MANUFACTURING, 2019, 28 :821-830

[24] Defect distribution and microstructure heterogeneity effects on fracture resistance and fatigue behavior of EBM Ti-6Al-4V [J].

Seifi, Mohsen ;

Salem, Ayman ;

Satko, Daniel ;

Shaffer, Joshua ;

Lewandowski, John J. .

INTERNATIONAL JOURNAL OF FATIGUE, 2017, 94 :263-287

[25] Surface roughness of Ti-6A1-4V parts obtained by SLM and EBM: Effect on the High Cycle Fatigue life [J].

Vayssette, Bastien ;

Saintier, Nicolas ;

Brugger, Charles ;

Elmay, Mohamed ;

Pessard, Ettienne .

7TH INTERNATIONAL CONFERENCE ON FATIGUE DESIGN, FATIGUE DESIGN 2017, 2018, 213 :89-97

[26]

Vtk.org, VISUALIZATION TOOLKI

[27]

Welsch G., 1994, Materials properties handbook: titanium alloys

[28]

Withers PJ, 2021, NAT REV METHOD PRIME, V1, DOI 10.1038/s43586-021-00015-4

[29]

Wohlers T.T., 2019, WOHLERS REPORT, P1

[30] EFFECT OF SURFACE ROUGHNESS ON VERY HIGH CYCLE FATIGUE BEHAVIOR OF Ti-6Al-4V ALLOY [J].

Zhu Lina ;

Deng Caiyan ;

Wang Dongpo ;

Hu Shengsun .

ACTA METALLURGICA SINICA, 2016, 52 (05) :583-591

← 1 2 3 →