A novel inorganic scintillator:: Lu2Si2O7:Ce3+ (LPS)

We have characterized the gamma and X-ray scintillation properties of Ce3+ doped Lu2Si2O7, a lutetium pyre-silicate (LPS) material. The rare earth ions are located in an octahedral site with C-2 symmetry. The compound exhibits chemical stability, transparency in a wide optical range and congruent melting, which allows growing of single crystals of good optical quality. The melting temperature is about 2000 degreesC, slightly lower than that of Lu2SiO5 (LSO). Two maxima at 305 nm and 355 nm are observed in the optical absorption spectrum. The emission spectrum of Ce3+ in LPS shows a broad band peaking at 380 nm. For a nominal Ce3+ atomic concentration of similar to0.01, under gamma-ray excitation we observe light yields in the range 13,000-23,000 photons/MeV, depending on the preparation atmosphere. The actual cerium concentration inside the crystal still needs to be determined. The scintillation decay time is around 30 ns and, in the first studies, neither a long component nor afterglow was observed.