Neutron and hard X-ray diffraction studies of the isothermal transformation kinetics in the research reactor fuel candidate U-8 wt% Mo

Exposing uranium-molybdenum alloys (UMo) retained in the gamma phase to elevated temperatures leads to transformation reactions during which the gamma-UMo phase decomposes into the thermal equilibrium phases, i.e. U2Mo and alpha-U. Since alpha-U is not suitable for a nuclear fuel exposed to high burn-up, it is necessary to retain the alpha-UMo phase during the production process of the fuel elements for modern high-performance research reactors. The present work deals with the isothermal transformation kinetics in U-8 wt% Mo alloys for temperatures between 673 and 798 K and annealing durations of up to 48 h. Annealed samples were examined at room temperature using either X-ray or neutron diffraction to determine the phase composition after thermal treatment, and in situ annealing studies disclosed the onset of phase decomposition. While for temperatures of 698 and 673 K the start of decomposition is delayed, for higher temperatures the first signs of transformation are already observable within 3 h of annealing. The typical C-shaped curves in a time-temperature-transformation (TTT) diagram for both the start and the end of phase decomposition could be determined in the observed temperature regime. Therefore, a revised TTT diagram for U-8 wt% Mo between 673 and 798 K and annealing durations of up to 48 h is proposed.