Preparation and tests for workability, compressive and bond strength of ultra-fine slag based geopolymer as concrete repairing agent

被引：97

作者：

Laskar, Sulaem Musaddiq ^{[1
]}

Talukdar, Sudip ^{[1
]}

机构：

[1] Indian Inst Technol Guwahati, Dept Civil Engn, Gauhati 781039, India

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2017年 / 154卷

关键词：

Ultra-fine ground granulated blast furnace slag; Flyash; Superplasticizer; Workability; Compressive strength; Bond strength; BLAST-FURNACE SLAG; FLY-ASH; METAKAOLIN GEOPOLYMER; MECHANICAL-PROPERTIES; PORTLAND-CEMENT; MORTAR; TEMPERATURE; ACTIVATION; AMBIENT;

D O I：

10.1016/j.conbuildmat.2017.07.187

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

In modern era, there is a need to develop sustainable concrete repairing material. This study aimed to develop ultra-fine blast furnace slag based geopolymer as concrete repairing agent. Sodium hydroxide activated geopolymer concrete mixes with various admixtures were prepared and tested to study fresh and hardened state properties including bond strength. The 1 day strength of ultra-fine blast furnace slag based geopolymer concrete was found to be about 60% of that at 28 days. Addition of flyash up to certain quantity level contributed towards achieving satisfactory workability, compressive and bond strength of the geopolymer concrete. Similar improvement in fresh and hardened state properties was also observed due to addition of superplasticizer at low dosage level. High alkali activator concentration led to loss of workability and strength of the geopolymer concrete. (C) 2017 Elsevier Ltd. All rights reserved.

引用

页码：176 / 190

页数：15

共 34 条

[1] Bond strength of PCC pavement repairs using metakaolin-based geopolymer mortar [J].

Alanazi, Hani ;

Yang, Mijia ;

Zhang, Dalu ;

Gao, Zhili .

CEMENT & CONCRETE COMPOSITES, 2016, 65 :75-82

[2] Alkaline activation of metakaolin and calcium hydroxide mixtures: influence of temperature, activator concentration and solids ratio [J].

Alonso, S ;

Palomo, A .

MATERIALS LETTERS, 2001, 47 (1-2) :55-62

[3] Alkali activation of a slag at ambient and elevated temperatures [J].

Altan, Ekin ;

Erdogan, Sinan T. .

CEMENT & CONCRETE COMPOSITES, 2012, 34 (02) :131-139

[4]

[Anonymous], 81121989 IS

[5]

[Anonymous], 17271967 IS

[6]

[Anonymous], 2004, 5161959 IS

[7]

[Anonymous], 2005, C882C882M13A ASTM, V04.02

[8]

[Anonymous], 2002, 27701967 IS

[9]

[Anonymous], 2002, 3831970 IS

[10] Very high strength (120 MPa) class F fly ash geopolymer mortar activated at different NaOH amount, heat curing temperature and heat curing duration [J].

Atis, C. D. ;

Gorur, E. B. ;

Karahan, O. ;

Bilim, C. ;

Ilkentapar, S. ;

Luga, E. .

CONSTRUCTION AND BUILDING MATERIALS, 2015, 96 :673-678

← 1 2 3 4 →