Corrosion Behaviour of a Zn/Zn-Al Double Coating in 5% NaCl Solution

被引：5

作者：

Weng, Tian-yu ^{[1
]}

Kong, Gang ^{[1
]}

Che, Chun-shan ^{[1
]}

Wang, Yan-qi ^{[1
]}

机构：

[1] South China Univ Technol, Sch Mat Sci & Engn, Guangzhou 510640, Guangdong, Peoples R China

来源：

INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE | 2018年 / 13卷 / 12期

关键词：

hot-dip Zn-5Al coating; EIS; corrosion; ZN-AL; COATED STEELS; MG COATINGS; ATMOSPHERIC CORROSION; INITIAL-STAGES; GALFAN ALLOY; RESISTANCE; PRODUCTS; SURFACE; FIELD;

D O I：

10.20964/2018.12.85

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

A new hot dip-galvanized Zn/Zn-5Al double coating was prepared by immersing steel into a molten pure zinc bath and then in a Zn-5Al alloy bath. The corrosion behaviour of the double coating was studied in 5% NaCl solution. The results showed that the coating consisted of a typical coating of Zn on the bottom with a Zn-Al layer on the top. The maximum thickness of the alloy coating was approximately 220 mu m. The neutral salt spray (NSS) test showed that the double coating was significantly effective for preventing corrosion. The corrosion resistance of the Zn-5Al alloy-coated steel was almost four times that of the Zn-coated steel according to the NSS test. The electrochemical tests indicated that the corrosion resistance of the Zn/Zn-Al double coating decreased with immersion time. However, the double coating also had a higher corrosion resistance and more negative corrosion potential compared with Zn-coated steel in 5% NaCl solution. SEM and XRD analyses revealed that the improved corrosion resistance of the Zn/Zn-5Al double coating was mainly due to the effect of Al on the corrosion products on the coating surface.

引用

页码：11882 / 11894

页数：13

共 34 条

[1] Corrosion mechanisms of Zn(Mg,Al) coated steel: 2. The effect of Mg and Al alloying on the formation and properties of corrosion products in different electrolytes
Azevedo, M. Salgueiro
Allely, C.
Ogle, K.
Volovitch, P.
[J]. CORROSION SCIENCE, 2015, 90 : 482 - 490
[2] Structure and Corrosion Behavior of Arc-Sprayed Zn-Al Coatings on Ductile Iron Substrate
Bonabi, Salar Fatoureh
Ashrafizadeh, Fakhreddin
Sanati, Alireza
Nahvi, Saied Mehran
[J]. JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2018, 27 (03) : 524 - 537
[3] Influence of Nd addition on the corrosion behavior of Zn-5%Al alloy in 3.5wt.% NaCl solution
Cao, Zujun
Kong, Gang
Che, Chunshan
Wang, Yanqi
[J]. APPLIED SURFACE SCIENCE, 2017, 426 : 67 - 76
[4] Characterization of corrosion products of Zn and Zn-Mg-Al coated steel in a marine atmosphere
Diler, E.
Rouvellou, B.
Rioual, S.
Lescop, B.
Vien, G. Nguyen
Thierry, D.
[J]. CORROSION SCIENCE, 2014, 87 : 111 - 117
[5] Nanoscopic view on the initial stages of corrosion of hot dip galvanized Zn-Mg-Al coatings
Duchoslav, J.
Arndt, M.
Steinberger, R.
Keppert, T.
Luckeneder, G.
Stellnberger, K. H.
Hagler, J.
Riener, C. K.
Angeli, G.
Stifter, D.
[J]. CORROSION SCIENCE, 2014, 83 : 327 - 334
[6] XPS study of the surface chemistry of conventional hot-dip galvanised pure Zn, galvanneal and Zn-Al alloy coatings on steel
Feliu, S
Barranco, V
[J]. ACTA MATERIALIA, 2003, 51 (18) : 5413 - 5424
[7] Corrosion resistance of Zn-Al co-cementation coatings on carbon steels
He, YD
Li, DZ
Wang, DR
Zhang, Z
Qi, HB
Gao, W
[J]. MATERIALS LETTERS, 2002, 56 (04) : 554 - 559
[8] Air permeability of the artificially synthesized Zn-Al-Mg alloy rusts
Ishikawa, Tatsuo
Ueda, Masato
Kandori, Kazuhiko
Nakayama, Takenori
[J]. CORROSION SCIENCE, 2007, 49 (06) : 2547 - 2556
[9] Corrosion monitoring of Zn and Zn-Al coated steels under wet-dry cyclic conditions using AC impedance method
Katayama, H
Tay, YC
Viloria, AS
Nishikata, A
Tsuru, T
[J]. MATERIALS TRANSACTIONS JIM, 1997, 38 (12): : 1089 - 1094
[10] Long-term atmospheric corrosion properties of thermally sprayed Zn, Al and Zn-Al coatings exposed in a coastal area
Katayama, Hideki
Kuroda, Seiji
[J]. CORROSION SCIENCE, 2013, 76 : 35 - 41

← 1 2 3 4 →