Comparative study on corrosion behavior of zinc-aluminum coated steel under thin electrolyte layers

被引：0
作者：
Zhao Xiaodong [1 ]
Yang Jie [1 ]
Xing Shaohua [2 ]
机构：
[1] Zhejiang Ocean Univ, Sch Electromech Engn, Zhoushan, Peoples R China
[2] Luoyang Ship Mat Res Inst, State Key Lab Marine Corros & Protect, Qingdao, Peoples R China
来源：
ADVANCED MATERIALS, PTS 1-4 | 2011年 / 239-242卷
关键词：
hot-dip coated steel; wet-dry condition; electrochemical impedance spectroscopy; corrosion monitoring; IMPEDANCE;
D O I：
10.4028/www.scientific.net/AMR.239-242.1335
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
Due to the excellent anticorrosion performance, zinc-aluminum coatings are widely used in a variety of structural applications, and most are exposed to atmosphere especially marine atmosphere. In this paper, weight loss experiment and electrochemical impedance spectroscopy technology were used to comparatively study the corrosion behavior of zinc-aluminum coatings in stimulant marine atmosphere. Experimental results show that the anticorrosion performance of GL coating was better than that of GF coating and the length of drying period had obviously influence on the corrosion behavior of GF and GL coating.
引用
收藏
页码：1335 / +
页数：2
相关论文
共 34 条
[21]   Formulation and study of corrosion prevention behavior of epoxy cerium nitrate–montmorillonite nanocomposite coated carbon steel [J].
E. Darmiani ;
I. Danaee ;
G. R. Rashed ;
D. Zaarei .
Journal of Coatings Technology and Research, 2013, 10 :493-502
[22]   Characterization of corrosion of X70 pipeline steel in thin electrolyte layer under disbonded coating by scanning Kelvin probe [J].
Fu, A. Q. ;
Tang, X. ;
Cheng, Y. F. .
CORROSION SCIENCE, 2009, 51 (01) :186-190
[23]   Electrochemical and surface analytical study of the corrosion behavior of mild steel with cathodically produced zinc phosphate coating [J].
Kellner, Florian J. J. ;
Schuetze, Katja ;
Kreutz, Christian ;
Virtanen, Sannakaisa .
SURFACE AND INTERFACE ANALYSIS, 2009, 41 (12-13) :911-917
[24]   Formulation and study of corrosion prevention behavior of epoxy cerium nitrate-montmorillonite nanocomposite coated carbon steel [J].
Darmiani, E. ;
Danaee, I. ;
Rashed, G. R. ;
Zaarei, D. .
JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, 2013, 10 (04) :493-502
[25]   Experimental study and finite element analysis of degradation behavior of epoxy zinc-rich coating system under stress corrosion [J].
Zhang, Hua ;
Huang, Xueming ;
Yang, Lei ;
Chen, Xiao ;
Lu, Jiakun .
JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2024, 38 (04) :618-636
[26]   COMPARATIVE STUDY OF CORROSION BEHAVIOR FOR PLASMA NITRIDED 1045 CARBON STEEL WITH AND WITHOUT PRETREATMENT OF SAND BLASTING [J].
Lu, Shijing ;
Zhao, Xiaobing ;
Miao, Bin ;
Song, Lu ;
Wei, Kunxia ;
Hu, Jing .
SURFACE REVIEW AND LETTERS, 2018, 25 (01)
[27]   Study of corrosion behavior of carbon steel under seawater film using the wire beam electrode method [J].
Liu, Zaijian ;
Wang, Wei ;
Wang, Jia ;
Peng, Xin ;
Wang, Yanhua ;
Zhang, Penghui ;
Wang, Haijie ;
Gao, Congjie .
CORROSION SCIENCE, 2014, 80 :523-527
[28]   Evaluation of the corrosion behavior of the polyester-coated galvanized steel subjected to SO2 gas under different relative humidities [J].
Reşit Yıldız ;
İlyas Dehri .
Protection of Metals and Physical Chemistry of Surfaces, 2013, 49 :740-748
[29]   Effect of Aluminum Flakes on Corrosion Protection Behavior of Water-Based Hybrid Zinc-Rich Coatings for Carbon Steel Substrate in NaCl Environment [J].
Boidot, Arthur ;
Gheno, Frederic ;
Bentiss, Fouad ;
Jama, Charafeddine ;
Vogt, Jean-Bernard .
COATINGS, 2022, 12 (10)
[30]   A Comparative Study on the Corrosion of Galvanized Steel under Simulated Rust Layer Solution with and without 3.5wt%NaCl [J].
Sun, Huyuan ;
Liu, Shuan ;
Sun, Lijuan .
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2013, 8 (03) :3494-3509
1234