Elevated temperature compressive properties of Zr-modified NiAl

Small Zr additions are known to substantially affect the deformation behavior and strength of polycrystalline NiAl, yet little information is currently available regarding the high-temperature properties of such alloys. Utilizing prealloyed powder technology, a series of four NiAl alloys have been produced containing from 0.05 to 0.7 at. pct Zr. The creep behavior of these alloys was characterized in compression between 1000 and 1400 K at strain rates ranging from similar to 0.1 to 10(-9) s(-1). All the Zr-modified alloys were significantly stronger than binary NiAl under fewer temperature and faster strain-rate conditions; however, the single-phase materials (Zr less than or equal to 0.1 at. pct) and binary NiAl had similar strengths at high temperatures and slow strain rates. The two-phase NiAl-Ni2AlZr alloys containing 0.3 and 0.7 at. pct Zr had nearly identical strengths. While the two-phase alloys were stronger than the single-phase materials at all test conditions, the degree of microstructural damage in the two-phase alloys due to internal oxidation during testing appeared to increase with Zr level. Balancing the poor oxidation behavior with the consistent strength advantage of the two-phase alloys, it is concluded that optimum elevated-temperature properties could be obtained in Heusler-strengthened NiAl containing between 0.1 and 0.3 at. pct Zr.