Phase equilibrium of Mg-Zn-La system in Mg-rich corner from 200 to 350 °C

被引:0
|
作者
Huang Mingli [1 ]
Li Hongxiao [1 ]
Ding Hua [1 ]
Ren Yuping [1 ]
Hao Shiming [1 ]
机构
[1] Northeastern Univ, Sch Met & Mat, Shenyang 110004, Peoples R China
来源
JOURNAL OF RARE EARTHS | 2007年 / 25卷
关键词
Mg-Zn-La system; phase equilibrium; T-phase; phase diagram; rare earths;
D O I
暂无
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
Alloys of Mg-Zn-La system in Mg rich corner were prepared, and the phase relationship was investigated at different temperatures such as 200, 300 and 350 C by scanning electron microscopy (SEM), X-ray diffraction (XRD) and electron probe microanalysis with energy dispersive X-ray spectroscopy (EPMA). Two types of phase equilibrium were identified at the different temperatures. One is two-phase equilibrium contained the Mg solid solution and T-phase. The other is three-phase equilibrium which contained the Mg solid solution, MgZn phase and T-phase. T-phase was stable as the temperature changed. The La content in T-phase is constant which is about 8 +/- 0.3% (atom fraction); but the Mg content and Zn content of that is changed, and the Zn content in T-phase was from 16.1% to 44%. The solubility of La in MgZn phase was increased from 1.2% to 1.6% as the temperature increasing from 200 to 350 degrees C.
引用
收藏
页码:519 / 522
页数:4
相关论文
共 50 条
  • [31] Experimental evidence of the Mg7(Zn, Ag)3 continuous solid solution in Mg-rich corner of Mg-Zn-Ag ternary system at 335 °C
    Zhao, Hong
    Yang, Bo
    Ren, Yuping
    Qin, Gaowu
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 789 : 991 - 995
  • [32] Phase equilibria and solidification of Mg-rich Mg-Al-Zn alloys
    Ohno, M
    Mirkovic, D
    Schmid-Fetzer, R
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 421 (1-2): : 328 - 337
  • [33] PHASE-EQUILIBRIA IN MG-RICH CORNER OF MAGNESIUM-COPPER-LEAD SYSTEM
    RAMBALDI, G
    MAZZONE, D
    MARAZZA, R
    DELFINO, S
    FERRO, R
    JOURNAL OF THE LESS-COMMON METALS, 1978, 59 (02): : 201 - 210
  • [34] Isothermal sections of the Mg-rich corner in the Mg-Sn-Y ternary system at 300 and 400 °C
    Zhao, H. D.
    Qin, G. W.
    Ren, Y. P.
    Pei, W. L.
    Guo, Y.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 481 (1-2) : 140 - 143
  • [35] TERNARY COMPOUNDS AND RELATIVE PHASE EQUILIBRIA IN THE Mg-RICH SIDE OF THE Mg-Zn-Ca SYSTEM
    Li Hongxiao
    Ma Qianqian
    Ren Yuping
    Jiang Min
    Qin Gaowu
    ACTA METALLURGICA SINICA, 2011, 47 (04) : 385 - 390
  • [36] Phase equilibria in Mg-rich corner of Mg-Ca-RE (RE=Gd, Nd) systems at 400 °C
    Fei, Hou-jun
    Xu, Guang-long
    Liu, Li-bin
    Bo, Hong
    Zeng, Li-jun
    Chen, Cui-ping
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2013, 23 (04) : 881 - 888
  • [37] Phases equilibrated with long-period stacking ordered phases in the Mg-rich corner of the Mg-Y-Zn system
    Yongxin Ruan
    Changrong Li
    Yuping Ren
    Xiaopan Wu
    R.Schmid-Fetzer
    Cuiping Guo
    Zhenmin Du
    Journal of Materials Science & Technology, 2021, 68 (09) : 147 - 159
  • [38] Phases equilibrated with long-period stacking ordered phases in the Mg-rich corner of the Mg-Y-Zn system
    Ruan, Yongxin
    Li, Changrong
    Ren, Yuping
    Wu, Xiaopan
    Schmid-Fetzer, R.
    Guo, Cuiping
    Du, Zhenmin
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2021, 68 : 147 - 159
  • [39] Phase equilibria and transformations in ternary Mg-rich Mg-Y-Zn alloys
    Groebner, J.
    Kozlov, A.
    Fang, X. Y.
    Geng, J.
    Nie, J. F.
    Schmid-Fetzer, R.
    ACTA MATERIALIA, 2012, 60 (17) : 5948 - 5962
  • [40] Experimental Study of the Solidification Microstructure in the Mg-Rich Corner of Mg-Al-Ce System
    Wong, Charlotte
    Styles, Mark J.
    Zhu, Suming
    Abbott, Trevor
    Nogita, Kazuhiro
    McDonald, Stuart D.
    StJohn, David H.
    Gibson, Mark A.
    Easton, Mark A.
    MAGNESIUM TECHNOLOGY 2018, 2018, : 79 - 85