The near-infrared broadband emission from bismuth-doped GeO2-WO3 and GeO2-BaO glasses

被引：10

作者：

Xia, Haiping ^{[1
]}

Wang, Xuejun ^{[1
]}

机构：

[1] Ningbo Univ, Lab Photoelect Mat, Ningbo 315211, Zhejiang, Peoples R China

来源：

SPECTROCHIMICA ACTA PART A-MOLECULAR AND BIOMOLECULAR SPECTROSCOPY | 2008年 / 70卷 / 01期

关键词：

Bi ions; GeO2-WO3; glasses; thermal stability; absorption edge; stimulated emission cross section;

D O I：

10.1016/j.saa.2007.07.020

中图分类号：

O433 [光谱学];

学科分类号：

0703 ; 070302 ;

摘要：

Glasses with the composition of (99.5- chi)GeO2-chi WO3-0.5Bi(2)O(3) (chi= 3, 6,9 mol%) and (99.5 psi)GeO2-psi BaO-0.5Bi(2)O(3) (psi =3, 6, 9 mol%) were prepared. Their thermal, emission and absorption measurements were carried out. The near-infrared super broadband emission of the prepared samples peak around 1.3 mu m was discovered. The results indicated, in GeO2-WO3-Bi2O3 glasses, increasing amount of WO3 brought about the broadening of FWHM, prolonging of lifetime and enhancing of thermal stabilities. While in GeO2-BaO-Bi2O3 glasses, concomitant with the increasing amount of BaO were the broadened FWHM as well as the prolonged lifetime. Red-shift tendency of absorption edges was discovered in both two groups of glasses indicating the Bi5+ ions might take responsibility for the broadband emission. (C) 2007 Elsevier B.V. All rights reserved.

引用

页码：122 / 125

页数：4

共 18 条

[1] A new fluorogermanate glass [J].

Cao, GX ;

Lin, FY ;

Hu, HF ;

Gan, FX .

JOURNAL OF NON-CRYSTALLINE SOLIDS, 2003, 326 :170-176

[2] Oxidation state and local coordination of chromium dopant in soda-lime-silicate and calcium-aluminate glasses [J].

Choi, YG ;

Kim, KH ;

Han, YS ;

Heo, J .

CHEMICAL PHYSICS LETTERS, 2000, 329 (5-6) :370-376

[3] Tungsten-tellurite glass:: a new candidate medium for Yb3+-doping [J].

Feng, X ;

Qi, CH ;

Lin, FY ;

Hu, HF .

JOURNAL OF NON-CRYSTALLINE SOLIDS, 1999, 256 :372-377

[4] Optical amplification in bismuth-doped silica glass [J].

Fujimoto, Y ;

Nakatsuka, M .

APPLIED PHYSICS LETTERS, 2003, 82 (19) :3325-3326

[5] Infrared luminescence from bismuth-doped silica glass [J].

Fujimoto, Y ;

Nakatsuka, M .

JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS, 2001, 40 (3B) :L279-L281

[6] NEAR-INFRARED LUMINESCENCE PROPERTIES OF THE LASER MATERIAL CR-Y2SIO5 [J].

HOMMERICH, U ;

EILERS, H ;

JACOBSEN, SM ;

YEN, WM ;

JIA, W .

JOURNAL OF LUMINESCENCE, 1993, 55 (5-6) :293-301

[7] NEAR-INFRARED EMISSION AT 1.35 MU-M IN CR DOPED GLASS [J].

HOMMERICH, U ;

EILERS, H ;

YEN, WM ;

HAYDEN, JS ;

ASTON, MK .

JOURNAL OF LUMINESCENCE, 1994, 60-1 :119-122

[8] Near infrared broadband emission of bismuth-doped aluminophosphate glass [J].

Meng, XG ;

Qiu, JR ;

Peng, MY ;

Chen, DP ;

Zhao, QZ ;

Jiang, XW ;

Zhu, CS .

OPTICS EXPRESS, 2005, 13 (05) :1628-1634

[9] Infrared broadband emission of bismuth-doped barium-aluminum-borate glasses [J].

Meng, XG ;

Qiu, JR ;

Peng, MY ;

Chen, DP ;

Zhao, QZ ;

Jiang, XW ;

Zhu, CS .

OPTICS EXPRESS, 2005, 13 (05) :1635-1642

[10] Charge transfer band observed in bismuth mixed-valence oxides, Bi1-xYxO1.5+delta(x = 0.3) [J].

Mizoguchi, H ;

Kawazoe, H ;

Hosono, H ;

Fujitsu, S .

SOLID STATE COMMUNICATIONS, 1997, 104 (11) :705-708

← 1 2 →