Exceptionally high cavitation erosion and corrosion resistance of a high entropy alloy

被引:174
作者
Nair, R. B. [1 ]
Arora, H. S. [1 ]
Mukherjee, Sundeep [2 ]
Singh, S. [3 ]
Singh, H. [3 ]
Grewal, H. S. [1 ]
机构
[1] Shiv Nadar Univ, Surface Sci & Tribol Lab, Dept Mech Engn, Gautam Budh Nagar, India
[2] Univ North Texas, Dept Mat Sci & Engn, Denton, TX 76203 USA
[3] Indian Inst Technol Roper, Dept Mech Engn, Rupnagar, India
关键词
Cavitation erosion-corrosion; High entropy alloy; Work-hardening; DEFORMATION MECHANISM; WEAR BEHAVIOR; MICROSTRUCTURE; 304-STAINLESS-STEEL; EVOLUTION; COATINGS;
D O I
10.1016/j.ultsonch.2017.09.044
中图分类号
O42 [声学];
学科分类号
070206 ; 082403 ;
摘要
Cavitation erosion and corrosion of structural materials are serious concerns for marine and offshore industries. Durability and performance of marine components are severely impaired due to degradation from erosion and corrosion. Utilization of advanced structural materials can play a vital role in limiting such degradation. High entropy alloys (HEM) are a relatively new class of advanced structural materials with exceptional properties. In the present work, we report on the cavitation erosion behavior of Al0.1CoCrFeNi HEA in two different media: distilled water with and without 3.5 wt% NaCl. For comparison, conventionally used stainless steel SS316L was also evaluated in identical test conditions. Despite lower hardness and yield strength, the HEA showed significantly longer incubation period and lower erosion-corrosion rate (nearly 1/4th) compared to SS316L steel. Enhanced erosion resistance of HEA was attributed to its high work-hardening behavior and stable passivation film on the surface. The Al0.1CoCrFeNi HEA showed lower corrosion current density, high pitting resistance and protection potential compared to SS316L steel. Further, HEA showed no evidence of intergranular corrosion likely due to the absence of secondary precipitates. Although, the degradation mechanisms (formation of pits and fatigue cracks) were similar for both the materials, the damage severity was found to be much higher for SS316L steel compared to HEA.
引用
收藏
页码:252 / 260
页数:9
相关论文
共 42 条
[1]  
[Anonymous], MED BIOL ENG COMPUT
[2]  
[Anonymous], CAVITATION RESISTANT
[3]  
[Anonymous], HIGH ENTROPY ALLOYS
[4]  
[Anonymous], CORROS SCI
[5]   Microstructural development in equiatomic multicomponent alloys [J].
Cantor, B ;
Chang, ITH ;
Knight, P ;
Vincent, AJB .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 375 :213-218
[6]   Microstructure and wear behavior of AlxCo1.5CrFeNi1.5Tiy high-entropy alloys [J].
Chuang, Ming-Hao ;
Tsai, Ming-Hung ;
Wang, Woei-Ren ;
Lin, Su-Jien ;
Yeh, Jien-Wei .
ACTA MATERIALIA, 2011, 59 (16) :6308-6317
[7]   Effect of hard second phase on cavitation erosion of Fe-Cr-Ni-C alloys [J].
Cuppari, MGD ;
Souza, RM ;
Sinatora, A .
WEAR, 2005, 258 (1-4) :596-603
[8]  
Dieter GE., 1976, MECH METALLURGY
[9]  
Franc J.-P., 2004, FUNDAMENTALS CAVITAT
[10]   Activation Energy and High Temperature Oxidation Behavior of Multi-Principal Element Alloy [J].
Grewal, Harpreet Singh ;
Sanjiv, Ramachandran Murali ;
Arora, Harpreet Singh ;
Kumar, Ram ;
Ayyagari, Aditya ;
Mukherjee, Sundeep ;
Singh, Harpreet .
ADVANCED ENGINEERING MATERIALS, 2017, 19 (11)