Investigation on mechanochemical behavior of Al/Mg-B2O3-Nb system reactive mixtures to synthesize niobium diboride

被引：17

作者：

Jafari, Majid ^{[1
]}

Tajizadegan, Hamid ^{[1
]}

Golabgir, Mohammad Hossein ^{[1
]}

Chami, Akbar ^{[1
]}

Torabi, Omid ^{[1
]}

机构：

[1] Islamic Azad Univ, Adv Mat Res Ctr, Dept Mat Engn, Najafabad Branch, Najafabad, Iran

来源：

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS | 2015年 / 50卷

关键词：

Mechanosynthesis; NbB2; Magnesiothermic reaction; Aluminothermic reaction; COMBUSTION SYNTHESIS; MA-SHS; NANOCOMPOSITE POWDER; NBB2; AIR; REDUCTION; NBC;

D O I：

10.1016/j.ijrmhm.2014.10.017

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Aluminum and magnesium were used in the M-B2O3-Nb (M = Al, Mg) system to synthesize niobium diboride (NbB2) via a mechanochemical process. The phase transformation and structural evaluation were investigated by means of X-ray diffractometry, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and differential thermal analysis techniques (DTA). Unlike thermodynamic possibility and DTA results, negligible aluminothermic reaction was occurred in the system and AINb(2) intermediate phase was formed during milling. On the other hand, nanostructure NbB2 was mechanosynthesized by the magnesiothermic reduction after 2.4 h of milling and the type of reactions was mechanically induced self-sustaining reaction (MSR). DTA results revealed that Mg-3(BO3)(2) was largely formed during the thermal process, while the quantity of this by-product extremely decreased during the mechanochemical synthesis and completely eliminated after 5 h of milling. Scanning and transmission electron microscopy observations confirmed that the range of particle size was within 100 nm. (C) 2014 Elsevier Ltd. All rights reserved.

引用

页码：86 / 92

页数：7

共 23 条

[21] Preparation of niobium borides NbB and NbB2 by self-propagating combustion synthesis
Yeh, C. L.
Chen, W. H.
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2006, 420 (1-2) : 111 - 116
[22] Preparation of TaB/TaB2/mullite composites by combustion synthesis involving aluminothermic reduction of oxide precursors
Yeh, C. L.
Kao, W. C.
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 615 : 734 - 739
[23] Formation of TiB2-Al2O3 and NbB2-Al2O3 composites by combustion synthesis involving thermite reactions
Yeh, C. L.
Li, R. F.
[J]. CHEMICAL ENGINEERING JOURNAL, 2009, 147 (2-3) : 405 - 411

← 1 2 3 →