Zn1-xCoxO Diluted Magnetic Semiconductor Bulk Prepared by Hot Pressing

被引：0
作者：
Lin Wensong [1 ]
Fang Ningxiang [2 ]
Ouyang Chenxin [1 ]
Wang Wei [1 ]
机构：
[1] Shanghai Univ Engn Sci, Sch Mat Engn, Shanghai 201620, Peoples R China
[2] Light Tough Composite Mat Co Ltd, Deqing 313219, Peoples R China
来源：
JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION | 2010年 / 25卷 / 03期
关键词：
hot pressing; diluted magnetic semiconductors; Zn1-xCoxO; DOPED ZNO; FERROMAGNETISM; FE;
D O I：
10.1007/s11595-010-0036-9
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Zn1-xCoxO diluted magnetic semiconductor bulks were prepared by hot pressing. Mixed powders of pure ZnO and CoO were compacted under pressure of 10 MPa at the temperature of 1 073 K. Then the samples were annealed in vacuum at the temperature from 673 K to 873 K for 10 h. The crystal structure and magnetic properties of Zn1-xCoxO bulks have been investigated by X-ray diffraction (XRD) and vibrating sample magnetometer (VSM). X-ray photoelectron spectroscopy (XPS) was used to study chemical valence of zinc and cobalt in the samples. The results showed that Zn1-xCoxO samples had c-axis oriented wurtzite symmetry, neither cobalt or cobalt oxide phase was found in the samples if x was less than 0.15. Zn and Co existed in Zn0.9Co0.1O sample in Zn2+ and Co2+ states. The results of VSM experiment proved the room temperature ferromagnetic properties (RTFP) of Co-doped ZnO samples. The saturation magnetization and the coercivity of Zn0.9Co0.1O sample, observed in the M-H curve, were about 0.20 emu/g and 200 Oe, respectively.
引用
收藏
页码：527 / 529
页数：3
相关论文
共 50 条
[21]   Variation of structural and magnetic properties with Co-doping in Zn1-xCoxO nanocrystals [J].
Li, Jian-jun ;
Hao, Wei-chang ;
Xu, Huai-zhe ;
Wang, Tian-min .
JOURNAL OF APPLIED PHYSICS, 2009, 105 (05)
[22]   Theoretical and experimental approaches to measuring mechanical properties of Zn1-xCoxO binary tetrahedral bulk semiconductors [J].
Asikuzun, E. ;
Ozturk, O. .
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2018, 29 (10) :7971-7978
[23]   Effect of crystallization quality on ferromagnetism in Zn1-xCoxO nanopowders [J].
Ma, Jing ;
Hao, Weichang ;
Luo, Ruiying ;
Xu, Huaizhe .
MATERIALS LETTERS, 2008, 62 (03) :403-406
[24]   Structure and properties variations in Zn1-xCoxO nanorods prepared by microwave-assisted hydrothermal method [J].
Fang, M. ;
Liu, Z. W. .
MATERIALS SCIENCE IN SEMICONDUCTOR PROCESSING, 2017, 57 :233-238
[25]   Structural and magnetic properties of Zn1-xCoxO (0<x≤0.30) nanoparticles [J].
Duan, L. B. ;
Chu, W. G. ;
Yu, J. ;
Wang, Y. C. ;
Zhang, L. N. ;
Liu, G. Y. ;
Liang, J. K. ;
Rao, G. H. .
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2008, 320 (08) :1573-1581
[26]   Effects of low concentration cobalt doping on the magnetic and optical properties of Zn1-xCoxO nanorods [J].
Kaur, T. ;
Singh, J. ;
Singh, B. ;
Pandey, V. S. ;
Singh, G. ;
Nayak, M. K. .
OPTOELECTRONICS AND ADVANCED MATERIALS-RAPID COMMUNICATIONS, 2017, 11 (5-6) :364-367
[27]   Direct evidence of defect coordination and magnetic interaction in local structure of wurtzite type Zn1-xCoxO thin films [J].
Satyarthi, P. ;
Ghosh, S. ;
Wang, Y. ;
Zhou, S. ;
Buerger, D. ;
Skorupa, I. ;
Schmidt, H. ;
Olivi, L. ;
Srivastava, P. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 670 :113-122
[28]   Magnetic Properties of Bulk Zn0.95-xMnxFe0.05O2 Prepared by Sol-gel Method and Subsequent Hot Pressing [J].
Lin, W. S. ;
Wen, C. H. ;
He, L. .
COMPUTATIONAL MATERIALS SCIENCE, PTS 1-3, 2011, 268-270 :356-359
[29]   Chemically Synthesized Ferromagnetic Zn1-xCoxO Nanocrystals: Raman Investigations [J].
Kashyap, Subhash C. ;
Bhatti, Kanwal Preet ;
Chaudhary, Sujeet ;
Pandya, Dinesh K. ;
Sharma, Shiv K. .
SYNTHESIS AND REACTIVITY IN INORGANIC METAL-ORGANIC AND NANO-METAL CHEMISTRY, 2009, 39 (04) :216-220
[30]   Magnetoresistance in laser-deposited Zn1-xCoxO thin films [J].
Kim, JH ;
Kim, H ;
Kim, D ;
Ihm, YE ;
Choo, WK .
PHYSICA B-CONDENSED MATTER, 2003, 327 (2-4) :304-306
12345