Zn1-xCoxO Diluted Magnetic Semiconductor Bulk Prepared by Hot Pressing

被引：0

作者：

Lin Wensong ^{[1
]}

Fang Ningxiang ^{[2
]}

Ouyang Chenxin ^{[1
]}

Wang Wei ^{[1
]}

机构：

[1] Shanghai Univ Engn Sci, Sch Mat Engn, Shanghai 201620, Peoples R China

[2] Light Tough Composite Mat Co Ltd, Deqing 313219, Peoples R China

来源：

JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION | 2010年 / 25卷 / 03期

关键词：

hot pressing; diluted magnetic semiconductors; Zn1-xCoxO; DOPED ZNO; FERROMAGNETISM; FE;

D O I：

10.1007/s11595-010-0036-9

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Zn1-xCoxO diluted magnetic semiconductor bulks were prepared by hot pressing. Mixed powders of pure ZnO and CoO were compacted under pressure of 10 MPa at the temperature of 1 073 K. Then the samples were annealed in vacuum at the temperature from 673 K to 873 K for 10 h. The crystal structure and magnetic properties of Zn1-xCoxO bulks have been investigated by X-ray diffraction (XRD) and vibrating sample magnetometer (VSM). X-ray photoelectron spectroscopy (XPS) was used to study chemical valence of zinc and cobalt in the samples. The results showed that Zn1-xCoxO samples had c-axis oriented wurtzite symmetry, neither cobalt or cobalt oxide phase was found in the samples if x was less than 0.15. Zn and Co existed in Zn0.9Co0.1O sample in Zn2+ and Co2+ states. The results of VSM experiment proved the room temperature ferromagnetic properties (RTFP) of Co-doped ZnO samples. The saturation magnetization and the coercivity of Zn0.9Co0.1O sample, observed in the M-H curve, were about 0.20 emu/g and 200 Oe, respectively.

引用

页码：527 / 529

页数：3

共 50 条

[11] Effect of annealing on Zn1-xCoxO thin films prepared by electrodeposition [J].

El Manouni, A. ;

Tortosa, M. ;

Manjon, F. J. ;

Mollar, M. ;

Mari, B. ;

Sanchez-Royo, J. F. .

MICROELECTRONICS JOURNAL, 2009, 40 (02) :268-271

[12] Influence of the surface structure on the magnetic properties of Zn1-xCoxO [J].

Ciatto, G. ;

Di Trolio, A. ;

Fonda, E. ;

Amidani, L. ;

Boscherini, F. ;

Thomasset, M. ;

Alippi, P. ;

Bonapasta, A. Amore .

APPLIED PHYSICS LETTERS, 2012, 101 (25)

[13] Low temperature heat capacity of bulk and nanophase ZnO and Zn1-xCoxO wurtzite phases [J].

Ma, Chengcheng ;

Shi, Quan ;

Woodfield, Brian F. ;

Navrotsky, Alexandra .

JOURNAL OF CHEMICAL THERMODYNAMICS, 2013, 60 :191-196

[14] Intrinsic magnetism of Zn1-xCoxO single-crystalline nanorods prepared by solvothermal method [J].

Zou, Youming ;

Qu, Zhe ;

Fang, Jun ;

Zhang, Yuheng .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2009, 321 (19) :3352-3355

[15] Magnetic properties of single crystalline Zn1-xCoxO thin films [J].

Sati, P. ;

Schaefer, S. ;

Morhain, C. ;

Deparis, C. ;

Stepanov, A. .

SUPERLATTICES AND MICROSTRUCTURES, 2007, 42 (1-6) :191-196

[16] Electron paramagnetic resonance in Zn1-xCoxO [J].

Acosta-Humanez, F. ;

Cogollo Pitalua, R. ;

Almanza, O. .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2013, 329 :39-42

[17] Structural, morphological and magnetic properties of Zn1-xCoxO prepared by sol-gel and hydrothermal method combined [J].

Hao Yongde ;

Zhou Legui ;

Li Jun ;

Hu Zuoqi .

JOURNAL OF SEMICONDUCTORS, 2016, 37 (11)

[18] Spin polarization of Zn1-xCoxO probed by magnetoresistance [J].

Li, Q. ;

Shen, T. T. ;

Dai, Z. K. ;

Cao, Y. L. ;

Yan, S. S. ;

Kang, S. S. ;

Dai, Y. Y. ;

Chen, Y. X. ;

Liu, G. L. ;

Mei, L. M. .

APPLIED PHYSICS LETTERS, 2012, 101 (17)

[19] The Influence of Annealing Atmosphere on the Properties of Zn1-xCoxO Powders as Seen by EPR Spectroscopy [J].

Popa, A. ;

Toloman, D. ;

Raita, O. ;

Stan, M. ;

Biris, A. R. ;

Giurgiu, L. M. .

PROCESSES IN ISOTOPES AND MOLECULES (PIM 2013), 2013, 1565 :246-249

[20] Influence of the developing magnetic order on the transport properties of epitaxial Zn1-xCoxO films [J].

Ye, S. ;

Ney, V. ;

Kammermeier, T. ;

Ollefs, K. ;

Zhou, S. ;

Schmidt, H. ;

Ney, A. .

INTERNATIONAL CONFERENCE ON MAGNETISM (ICM 2009), 2010, 200

← 1 2 3 4 5 →