Effects of Impurity Oxygen Content in Raw Si Powder on Thermal and Mechanical Properties of Sintered Reaction-Bonded Silicon Nitrides

被引:49
作者
Kusano, Dai [1 ,2 ,3 ]
Adachi, Shigeru [3 ]
Tanabe, Gen [3 ]
Hyuga, Hideki [2 ]
Zhou, You [2 ]
Hirao, Kiyoshi [1 ,2 ]
机构
[1] Nagoya Inst Technol, Dept Frontier Mat, Showa Ku, Nagoya, Aichi 4668555, Japan
[2] Natl Inst Adv Ind Sci & Technol, Moriyama Ku, Nagoya, Aichi 4638560, Japan
[3] Japan Fine Ceram Co Ltd, Sendai, Miyagi 9813203, Japan
关键词
GRAIN-GROWTH; CONDUCTIVITY; BETA-SI3N4; CERAMICS; SI3N4; LATTICE; DIFFUSIVITY; ADDITIVES; CRYSTAL;
D O I
10.1111/j.1744-7402.2011.02618.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Sintered reaction-bonded silicon nitrides (SRBSNs) were fabricated from commercially available low-grade Si powder containing 1.6 mass% of impurity oxygen and 500 ppm of metallic impurities. Powder compacts of the raw Si powder doped with Y2O3 and MgO/MgSiN2 as sintering additives were nitrided at 1400 degrees C for 8 h under a N2 pressure of 0.1 MPa, followed by postsintering at 1900 degrees C for 6 h under a N2 pressure of 0.9 MPa. The SRBSN with Y2O3 and MgO as sintering additives had a four-point bending strength of about 700 MPa, but lower thermal conductivity of about 89 W/m/K. Thermal conductivity could be improved to over 100 W/m/K without degrading the bending strength by replacing MgO with MgSiN2. It is thought that MgSiN2 decreased the amount of oxygen in the liquid phase formed during sintering, which resulted in reduced lattice oxygen content in the developed beta-Si3N4 grains. In addition, the SRBSN with Y2O3 and MgSiN2 additive exhibited high fracture toughness of about 9 MPa m1/2. These good properties were equivalent to those of the SRBSN fabricated by using a reagent-grade high-purity Si powder containing only 0.3 mass% of impurity oxygen.
引用
收藏
页码:229 / 238
页数:10
相关论文
共 36 条
[21]   Preparation of fine AlN powders by wet ball-milling and their characterization [J].
Nagai, Y ;
Lai, GC .
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1997, 105 (01) :6-10
[22]   FLASH METHOD OF DETERMINING THERMAL DIFFUSIVITY, HEAT CAPACITY, AND THERMAL CONDUCTIVITY [J].
PARKER, WJ ;
JENKINS, RJ ;
ABBOTT, GL ;
BUTLER, CP .
JOURNAL OF APPLIED PHYSICS, 1961, 32 (09) :1679-&
[23]   QUANTITATIVE PHASE-ANALYSIS OF SI3N4 BY X-RAY-DIFFRACTION [J].
PIGEON, RG ;
VARMA, A .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1992, 11 (20) :1370-1372
[24]   NONMETALLIC CRYSTALS WITH HIGH THERMAL-CONDUCTIVITY [J].
SLACK, GA .
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 1973, 34 (02) :321-335
[25]   Experimental and computational study of grain growth in AlN based ceramics [J].
Tajika, M ;
Matsubara, H ;
Rafaniello, W .
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1997, 105 (11) :928-933
[26]   Control of instability of Si3N4 during pressureless sintering [J].
Wada, S .
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2001, 109 (10) :803-808
[27]  
WATARI K, 1989, NIPPON SERAM KYO GAK, V97, P56, DOI 10.2109/jcersj.97.56
[28]   Hot isostatic pressing to increase thermal conductivity of Si3N4 ceramics [J].
Watari, K ;
Hirao, K ;
Brito, ME ;
Toriyama, M ;
Kanzaki, S .
JOURNAL OF MATERIALS RESEARCH, 1999, 14 (04) :1538-1541
[29]   High thermal conductivity non-oxide ceramics [J].
Watari, K .
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2001, 109 (01) :S7-S16
[30]   Thermal conductivity of β-Si3N4 single crystal [J].
Watari, K ;
Li, BC ;
Pottier, L ;
Fournier, D ;
Toriyama, M .
ELECTROCERAMICS IN JAPAN III, 2000, 181-1 :239-242