Low temperature synthesis of MgTa2O6 powders

被引：8

作者：

Navale, SC

Samuel, V

Ravi, V ^{[1
]}

机构：

[1] Natl Chem Lab, Phys & Mat Chem Div, Pune 411008, Maharashtra, India

[2] Natl Chem Lab, Catalysis Div, Pune 411008, Maharashtra, India

[3] Natl Chem Lab, Polymer Sci & Engn Div, Pune 411008, Maharashtra, India

来源：

MATERIALS LETTERS | 2005年 / 59卷 / 29-30期

关键词：

ceramics; oxides; X-ray diffraction; electron microscopy; magnesium tantalate;

D O I：

10.1016/j.matlet.2005.07.035

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A combination of digestion and further low temperature calcination to crystallize the product is employed to prepare MgTa2O6 (MT) ceramics. Freshly prepared niobium hydroxide gel is mixed with magnesium hydroxide thoroughly and allowed to react at 100 degrees C under refluxing and stirring conditions for 6-12 h. The X-ray amorphous product so formed is heated at 550 degrees C to form crystalline MgTa2O6. This is the lowest temperature so far reported for the formation of MgTa2O6. For comparison, MT powders were also prepared by the traditional solid state method. Transmission electron microscope (TEM) investigations revealed that the average particle size is 40 nm for the low temperature calcined powders. (C) 2005 Elsevier B.V. All rights reserved.

引用

页码：3926 / 3928

页数：3

共 11 条

[1] Synthesis of nanocrystalline Mn3O4 at 100 °C [J].