Structural and photoelectrochemical characterization of Cu2SnSe3 thin films fabricated by electrochemical co-deposition and selenization

The Cu-Sn alloy as a precursor for Cu2SnSe3 (CTSe) thin films was electrochemically co-deposited from a modified electrolyte solution using magnetic steering. The Cu-Sn film on the Mo/glass substrate was continuous, smooth and contained no organic contaminants according to Raman spectroscopy. The current efficiency of Cu-Sn electrodeposition in the solution was about 90%, i.e. significantly higher than that previously reported. The Cu-Sn films with the Cu/Sn ratio in the range of 1.6-2.3 were selenized at temperatures of 350, 400, 450, 500 and 560 degrees C. The synthesized CTSe films were characterised by XRD, SEM, EDX and Raman spectroscopy. The photo-activity of the films was assessed by photoelectrochemical measurements in a 0.2 M Eu(NO3)(3) aqueous solution. The conducted investigations revealed that the Cu2SnSe3 film with Cu/Sn = 1.9 selenized at a temperature of 500 degrees C demonstrated the best photoelectrochemical response and presented p type doping. The photo-activity of the film increased after additional annealing in air at a temperature of 200 degrees C. Raman spectroscopy studies of Cu2SnSe3 thin films revealed a rather insignificant difference between the spectra of cubic and monoclinic polymorphs, however, one of the bands in the low energy region could be treated as a marker of the monoclinic phase. The Raman spectra evidenced that nearly all of the studied Cu2SnSe3 films contained SnSe2 the presence of which is detrimental for the photovoltaic characteristics of both Cu2SnSe3 and Cu2ZnSnSe4. (C) 2018 Elsevier B.V. All rights reserved.