Real-time Detection of CMAS Corrosion Failure in APS Thermal Barrier Coatings Under Thermal Shock

被引:31
作者
Zhu, W. [1 ,2 ]
Li, Z. Y. [1 ,2 ]
Yang, L. [1 ,2 ]
Zhou, Y. C. [1 ,2 ]
Wei, J. F. [1 ,2 ]
机构
[1] Xiangtan Univ, Sch Mat Sci & Engn, Key Lab Key Film Mat & Applicat Equipment Hunan P, Xiangtan 411105, Hunan, Peoples R China
[2] Xiangtan Univ, Sch Mat Sci & Engn, Key Lab Low Dimens Mat & Applicat Technol, Minist Educ, Xiangtan 411105, Hunan, Peoples R China
基金
中国国家自然科学基金;
关键词
Thermal barrier coatings; CMAS corrosion; Failure mechanism; Acoustic emission; Infrared thermography; MAGNESIUM-ALUMINO-SILICATE; ZIRCONIA COATINGS; DAMAGE EVOLUTION; DEGRADATION; MECHANISMS; TEMPERATURE; RESISTANCE; BEHAVIOR; DELAMINATION; DEPOSITS;
D O I
10.1007/s11340-020-00603-7
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Calcium-magnesium-alumina-silicate (CMAS) corrosion has been regarded as the most important factor that leads to the degradation of thermal barrier coatings (TBCs). The failure mechanism of TBCs attacked by CMAS corrosion in the actual service conditions is still not clear due to the lack of an environmental simulator and nondestructive testing techniques. To solve the above problems, a real-time acoustic emission method combined with infrared thermography are developed to investigate the failure mechanism of TBCs attacked by CMAS corrosion. The results show that the acoustic emission signal spectrum only depends on the failure mode of the TBCs, and five failure modes are identified: surface vertical cracks, sliding interfacial cracks, opening interfacial cracks, substrate deformation and noise. The lifetime of TBCs attacked by CMAS corrosion is 40 thermal shock cycles, which is nearly six times lower than that of TBCs without CMAS corrosion (350 cycles). Conclusions: The failure mechanism of the former is interlaminar cracking and delamination in the ceramic coating; while that for the latter is interfacial delamination in the vicinity of thermal growth oxide.
引用
收藏
页码:775 / 785
页数:11
相关论文
共 46 条
[21]   Failure of Thermal Barrier Coatings Subjected to CMAS Attack [J].
Li, L. ;
Hitchman, N. ;
Knapp, J. .
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2010, 19 (1-2) :148-155
[22]   Effect of CMAS infiltration on radiative transport through an EB-PVD thermal barrier coating [J].
Li, Li ;
Clarke, David R. .
INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2008, 5 (03) :278-288
[23]   High-Temperature Corrosion of EB-PVD Yttria Partially Stabilized Zirconia Thermal Barrier Coatings with an Artificial Volcanic Ash Overlay [J].
Mechnich, Peter ;
Braue, Wolfgang ;
Schulz, Uwe .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2011, 94 (03) :925-931
[24]   Materials science - Thermal barrier coatings for gas-turbine engine applications [J].
Padture, NP ;
Gell, M ;
Jordan, EH .
SCIENCE, 2002, 296 (5566) :280-284
[25]   The Hotter the Engine, the Better [J].
Perepezko, John H. .
SCIENCE, 2009, 326 (5956) :1068-1069
[26]   Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings [J].
Rabiei, A ;
Evans, AG .
ACTA MATERIALIA, 2000, 48 (15) :3963-3976
[27]   Thermographic analysis and modelling of the delamination crack growth in a thermal barrier coating on Fecralloy substrate [J].
Schweda, Mario ;
Beck, Tilmann ;
Offermann, Marita ;
Singheiser, Lorenz .
SURFACE & COATINGS TECHNOLOGY, 2013, 217 :124-128
[28]   A novel test approach for plasma-sprayed coatings tested simultaneously under CMAS and thermal gradient cycling conditions [J].
Steinke, Tanja ;
Sebold, Doris ;
Mack, Daniel E. ;
Vassen, Robert ;
Stoever, Detlev .
SURFACE & COATINGS TECHNOLOGY, 2010, 205 (07) :2287-2295
[29]   Thermal barrier coatings for heat engines [J].
Troczynski, T ;
Cockcroft, S ;
Wong, H .
ADVANCED CERAMIC MATERIALS: APPLICATIONS OF ADVANCED MATERIALS IN A HIGH-TECH SOCIETY I, 1996, 122-1 :451-462
[30]   Calcium-magnesium-alumino-silicate (CMAS) degradation of EB-PVD thermal barrier coatings: Characterization of CMAS damage on ex-service high pressure blade TBCs [J].
Vidal-Setif, M. H. ;
Chellah, N. ;
Rio, C. ;
Sanchez, C. ;
Lavigne, O. .
SURFACE & COATINGS TECHNOLOGY, 2012, 208 :39-45