Experimental Study on Preparation of Mullite Decorative Materials

被引：0
|
作者：
Ma, J. S. [1 ]
Zhou, M. M. [1 ]
Cai, H. Q. [1 ]
Bai, R. S. [1 ]
机构：
[1] Hebei Univ Architecture, Dept Civil Engn, Zhangjiakou 075000, Peoples R China
来源：
PROCEEDINGS OF THE 2ND ANNUAL INTERNATIONAL CONFERENCE ON ADVANCED MATERIAL ENGINEERING (AME 2016) | 2016年 / 85卷
关键词：
Mullite; Decorative materials; Preparation;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The pouring vibration method is adopted to prepare a fireproof, durable and decorative wall panel, whose materials for preparation are mullite, cement, powder, glass beads, cellulose, pigments and waterproofing agent. The test result shows that the greatest dosage of raw materials for preparing decorative plates is mullite : cement : glass beads : powder : cellulose : pigment : waterproofing agent = 100 : 60 : 20 : 5 : 1 : 10 : 5. Under the ratio, the decorative wall panel gained the apparent density of 942kg/m(3), compressive strength of 7.6MPa, flexural strength of 2.3MPa and water absorption of 6.5%.
引用
收藏
页码：99 / 104
页数：6
相关论文
共 50 条
  • [31] The effect of mullite on the mechanical properties and thermal shock behaviour of alumina-mullite refractory materials
    Aksel, C
    CERAMICS INTERNATIONAL, 2003, 29 (02) : 183 - 188
  • [32] Preparation of mullite fibres by sol-gel processes using aluminium carboxylates and tetraethylorthosilicate
    Tan, H. B.
    Zhang, Y. B.
    Ding, Y. P.
    Yang, J. F.
    MATERIALS SCIENCE AND TECHNOLOGY, 2011, 27 (02) : 568 - 572
  • [33] Preparation and corrosion of mullite thin film on β-sialon ceramics
    Noritake, Yasunobu
    Kiyono, Hajime
    Shimada, Shiro
    Key Engineering Materials, 2009, 403 : 135 - 138
  • [34] Preparation cordierite-mullite composites with iron tailing
    Li, Fengfeng
    Yang, Weichao
    Zhang, Mingxi
    Zhang, Lifang
    Shen, Yi
    BIOTECHNOLOGY, CHEMICAL AND MATERIALS ENGINEERING, PTS 1-3, 2012, 393-395 : 902 - +
  • [35] Preparation of zirconia-toughened mullite with dissociated zircon
    S. Bhattacharjee
    R. K. Galgali
    S. K. Singh
    Mining, Metallurgy & Exploration, 2001, 18 : 200 - 202
  • [36] Preparation of Anorthite/Mullite In Situ and Phase Transformation in Porcelain
    Lin, Shao-Min
    Yu, Ya-Ling
    Zhong, Ming-Feng
    Yang, Huan
    Liu, Yang
    Li, Hang
    Zhang, Chen-Yang
    Zhang, Zhi-Jie
    MATERIALS, 2023, 16 (04)
  • [37] Preparation of mesoporous mullite fibers by selective leaching method
    Takei, T
    Hayashi, S
    Yasumori, A
    Okada, K
    PROCESSING AND FABRICATION OF ADVANCED MATERIALS VI, VOLS 1 & 2, 1998, : 901 - 906
  • [38] Preparation of zirconia-mullite composites by an infiltration route
    Park, HC
    Yang, TY
    Yoon, SY
    Stevens, R
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 405 (1-2): : 233 - 238
  • [39] Preparation of mullite by corrosion of aluminum in acetic acid solution
    Seri, Osami
    Wada, Yoshiyuki
    Keikinzoku/Journal of Japan Institute of Light Metals, 2012, 62 (09): : 327 - 330
  • [40] Preparation of mullite powders by sol-gel methods
    Jin, XH
    Gao, L
    Guo, JK
    JOURNAL OF INORGANIC MATERIALS, 2001, 16 (03) : 555 - 558
12345