Smoke, CO, and CO2 measurements and evaluation using different fire testing techniques for flame retardant unsaturated polyester resin formulations

被引:56
作者
Nazare, S. [1 ]
Kandola, B. K. [1 ]
Horrocks, A. R. [1 ]
机构
[1] Univ Bolton, Ctr Mat Res & Innovat, Bolton BL3 5AB, England
基金
英国工程与自然科学研究理事会;
关键词
unsaturated polyester; nanocomposites; flame retardants; smoke suppressants; toxicity; fire conditions;
D O I
10.1177/0734904107087818
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Smoke is considered to be the main fire hazard but its production depends on major variables, principally the chemical character and the burning rate of the polymer plus the availability of oxygen and hence ventilation. The main aim of this work is to study the effect of smoke suppressants on flammability and smoke production of flame retarded unsaturated polyester resin-nanocomposites using four different testing regimes representing different fire scenarios. Samples containing zinc borate, zinc stannates, ammonium polyphosphate with and without nanoclay are analyzed for smoke generation using cone calorimetry (well-ventilated fire), a tube furnace (fully developed fire), and a smoke density chamber (under-ventilated fire). Carbon monoxide (CO) and carbon dioxide (CO2) measurements using thermogravimetry-evolved gas analysis (TG-EGA), cone calorimetry, and tube furnace have also been analyzed and compared. Results have confirmed that the production of smoke, CO, and CO2 depend upon smoke suppressants and fire conditions used during testing samples. From this study it is evident that tin additives have very little influence on flammability of unsaturated polyester resin but they reduce smoke formation. The slight flame retardant action of the Res/APP/ZB sample is due to enhanced cross-linking of APP in the presence of zinc borate, whereas zinc stannates do not promote cross-linking of APP and hence show no improvement in flame retardancy. Finally, the presence of nanoclay in flame retarded resin shows significant reduction in smoke formations in both well-ventilated and under-ventilated fire condition. However, in the presence of smoke suppressants used in this study, the nanoclay is not instrumental in further suppressing smoke formation.
引用
收藏
页码:215 / 242
页数:28
相关论文
共 30 条
[1]   Inorganic tin compounds as flame retardants and smoke suppressants for polyester thermosets [J].
Atkinson, PA ;
Haines, PJ ;
Skinner, GA .
THERMOCHIMICA ACTA, 2000, 360 (01) :29-40
[2]   The mechanism of action of tin compounds as flame retardants and smoke suppressants for polyester thermosets [J].
Atkinson, PA ;
Haines, PJ ;
Skinner, GA .
POLYMER DEGRADATION AND STABILITY, 2001, 71 (03) :351-360
[3]  
BABRAUSKAS V, 1992, P INT C FIR MAT, P155
[4]   A study of the combustion and fire-retardance behaviour of unsaturated polyester/phenolic resin blends [J].
Chiu, HT ;
Chiu, SH ;
Jeng, RE ;
Chung, JS .
POLYMER DEGRADATION AND STABILITY, 2000, 70 (03) :505-514
[5]   Effects of tin additives on the flammability and smoke emission characteristics of halogen-free ethylene-vinyl acetate copolymer [J].
Cross, MS ;
Cusack, PA ;
Hornsby, PR .
POLYMER DEGRADATION AND STABILITY, 2003, 79 (02) :309-318
[6]   AN INVESTIGATION OF INORGANIC TIN FLAME RETARDANTS WHICH SUPPRESS SMOKE AND CARBON-MONOXIDE EMISSION FROM BURNING BROMINATED POLYESTER RESINS [J].
CUSACK, PA ;
MONK, AW ;
PEARCE, JA ;
REYNOLDS, SJ .
FIRE AND MATERIALS, 1989, 14 (01) :23-29
[8]   Zinc hydroxystannate as an alternative synergist to antimony trioxide in polyester resins containing halogenated flame retardants [J].
Cusack, PA ;
Heer, MS ;
Monk, AW .
POLYMER DEGRADATION AND STABILITY, 1997, 58 (1-2) :229-237
[9]  
CUSACK PA, 1998, PLASTICS ADDITIVES A
[10]  
EDELSON D, 1982, S INT COMBUSTION, V19, P807