Preparation of oriented BiVO4 thin film by chemical bath deposition

被引：0

作者：

Liu Jing-Bing ^{[1
]}

Wang Hao ^{[1
]}

Zhang Hui-Ming ^{[1
]}

Zhang Wen-Xiong ^{[1
]}

Yan Hui ^{[1
]}

机构：

[1] Beijing Univ Technol, Coll Mat Sci & Engn, Beijing 100022, Peoples R China

来源：

CHINESE JOURNAL OF INORGANIC CHEMISTRY | 2007年 / 23卷 / 07期

关键词：

BiVO4; film; chemical bath deposition; orientation;

D O I：

暂无

中图分类号：

O61 [无机化学];

学科分类号：

070301 ; 081704 ;

摘要：

Highly oriented BiVO4 films were synthesized on glass substrates by modified chemical bath deposition (CBD). The influence of the deposition parameters as temperature and time of deposition on the rate of process and the quality of BiVO4 films was studied by XRD, Raman Spectroscopy and SEM. The film deposited at 90 degrees C for 12 h was dense and uniform. The BiVO4 thin film under this optimal depositing conditions was consisted of octagonal crystalline grains in a narrow size distribution with an average size of about 7 mu m, showing a (004) preferential orientation.

引用

页码：1299 / 1302

页数：4

共 17 条

[1] MOCVD growth of (100)-oriented CeO2 thin films on hydrogen-terminated Ssi(100) substrates [J].

Ami, T ;

Suzuki, M .

MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 1998, 54 (1-2) :84-91

[2] FERROELASTICITY IN BIVO4 [J].

BIERLEIN, JD ;

SLEIGHT, AW .

SOLID STATE COMMUNICATIONS, 1975, 16 (01) :69-70

[3] BiVO4 thin film preparation by metalorganic decomposition [J].

Galembeck, A ;

Alves, OL .

THIN SOLID FILMS, 2000, 365 (01) :90-93

[4]

Izaki M, 2001, ADV MATER, V13, P142, DOI 10.1002/1521-4095(200101)13:2<142::AID-ADMA142>3.0.CO

[5]

2-9

[6] A novel aqueous process for preparation of crystal form-controlled and highly crystalline BiVO4 powder from layered vanadates at room temperature and its photocatalytic and photophysical properties [J].

Kudo, A ;

Omori, K ;

Kato, H .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1999, 121 (49) :11459-11467

[7] PROMINENT FERROELASTIC DOMAIN-WALLS IN BIVO4 CRYSTAL [J].

LIM, AR ;

CHOH, SH ;

JANG, MS .

JOURNAL OF PHYSICS-CONDENSED MATTER, 1995, 7 (37) :7309-7323

[8] Hydrothermal preparation of BiVO4 powders [J].

Liu, JB ;

Wang, H ;

Wang, S ;

Yan, H .

MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2003, 104 (1-2) :36-39

[9]

MARCIA C, 2002, THIN SOLID FILMS, V406, P93

[10] DEPOSITION OF CADMIUM CHALCOGENIDE THIN-FILMS BY A SOLUTION GROWTH TECHNIQUE USING TRIETHANOLAMINE AS A COMPLEXING AGENT [J].

MONDAL, A ;

CHAUDHURI, TK ;

PRAMANIK, P .

SOLAR ENERGY MATERIALS, 1983, 7 (04) :431-438

← 1 2 →