Research on Binderless Tungsten Carbide Prepared by Spark Plasma Sintering

被引：7

作者：

Li, Xiaoqiang ^{[1
]}

Xiao, Zhangyi ^{[1
]}

Yang, Chao ^{[1
]}

Qu, Shengguan ^{[1
]}

机构：

[1] S China Univ Technol, Sch Mech & Automot Engn, Guangzhou 510640, Guangdong, Peoples R China

来源：

ADVANCES IN ENGINEERING DESIGN AND OPTIMIZATION, PTS 1 AND 2 | 2011年 / 37-38卷

关键词：

Pure WC powders; Particle size; Spark plasma sintering; GROWTH;

D O I：

10.4028/www.scientific.net/AMM.37-38.980

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Commerical pure WC powders of 0.2, 0.4, 0.8, 2.0 and 3.0 mu m in diameter were sintered by spark plasma sintering process at 1300 degrees C, respectively. By analyzing the XRD patterns of the initial powders and the microstructure of the sintered samples, it is affirmed that the powders with an average size of 0.8 pm exhibits the best activity and sintering property. To optimize sintering temperature, the sintering of 0.8 mu m powders was carried out at 1200-1700 degrees C. The specimen sintered at 1300 degrees C has a density of 15.49 g/cm(3) and an average grain size of about 0.7 mu m, and exhibits the most excellent mechanical properties. The corresponding Vickers hardness and transverse rupture strength are 2469 HV and 1656 MPa, respectively.

引用

页码：980 / 984

页数：5

共 50 条

[1] Bulk ultrafine binderless WC prepared by spark plasma sintering [J].

Huang, B ;

Chen, LD ;

Bai, SQ .

SCRIPTA MATERIALIA, 2006, 54 (03) :441-445

[2] Consolidation and properties of ultrafine binderless cemented carbide by spark plasma sintering [J].

Liu Xiangqing ;

Lin Tao ;

Shao Huiping ;

Guo Zhimeng ;

Luo Ji ;

Hao Junjie .

RARE METALS, 2008, 27 (03) :320-323

[3] Consolidation and properties of ultrafine binderless cemented carbide by spark plasma sintering [J].

LIU Xiangqing LIN Tao Shao Huiping GUO Zhimeng LUO Ji HAO Junjie School of Materials Science and EngineeringUniversity of Science and Technology BeijingBeijing China .

Rare Metals, 2008, (03) :320-323

[4] Microstructures of binderless tungsten carbides sintered by spark plasma sintering process [J].

Cha, SI ;

Hong, SH .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 356 (1-2) :381-389

[5] Effect of ZrC nano-powder addition on the microstructure and mechanical properties of binderless tungsten carbide fabricated by spark plasma sintering [J].

Ren, Xiaoyong ;

Peng, Zhijian ;

Wang, Chengbiao ;

Fu, Zhiqiang ;

Qi, Longhao ;

Miao, Hezhuo .

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2015, 48 :398-407

[6] Spark plasma sintering of TiC ceramic with tungsten carbide as a sintering additive [J].

Cheng, Lixia ;

Xie, Zhipeng ;

Liu, Guanwei .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2013, 33 (15-16) :2971-2977

[7] Adhesive wear performance of self-lubricating functionally graded cemented tungsten carbide prepared by spark plasma sintering [J].

Parihar, Rityuj Singh ;

Sahu, Raj Kumar ;

Setti, Srinivasu Gangi .

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2022, 104

[8] Spark plasma sintering of tantalum carbide [J].

Khaleghi, Evan ;

Lin, Yen-Shan ;

Meyers, Marc A. ;

Olevsky, Eugene A. .

SCRIPTA MATERIALIA, 2010, 63 (06) :577-580

[9] Spark plasma sintering of tungsten carbide nanopowders obtained through DC arc plasma synthesis [J].

Chuvil'deev, V. N. ;

Blagoveshchenskiy, Yu. V. ;

Nokhrin, A. V. ;

Boldin, M. S. ;

Sakharov, N. V. ;

Isaeva, N. V. ;

Shotin, S. V. ;

Belkin, O. A. ;

Popov, A. A. ;

Smirnova, E. S. ;

Lantsev, E. A. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 708 :547-561

[10] Material properties of tungsten carbide-alumina composites fabricated by spark plasma sintering [J].

Chen, Wei-Hsio ;

Lin, Hao-Tung ;

Nayak, Pramoda K. ;

Huang, Jow-Lay .

CERAMICS INTERNATIONAL, 2014, 40 (09) :15007-15012

← 1 2 3 4 5 →