Influence of N2 Partial Pressure of Zirconium Nitride by Magnetron Sputtering on the Bonding Strength of Titanium/Porcelain

被引:0
作者
Wang Shushu [1 ]
Wu Xiangjun [2 ]
Guang Hanbing [3 ]
Zhou Shu [1 ]
Zhang Wenyan [2 ]
Zhang Feimin [1 ]
机构
[1] Nanjing Med Univ, Inst Stomatol, Nanjing 210029, Peoples R China
[2] Southeast Univ, Nanjing 211189, Peoples R China
[3] Stomatol Hosp Jiangsu Prov, Denture Machining Ctr, Nanjing 210029, Peoples R China
关键词
zirconium nitride (ZrN); magnetron sputtering; N-2 partial pressure; titanium porcelain; bonding strength; TITANIUM-PORCELAIN; FILMS; SPECTROMETRY; OXIDATION;
D O I
暂无
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The influence of zirconium nitride (ZrN) deposited by magnetron sputtering under different N-2 partial pressure on the bonding strength of titanium porcelain was investigated. 60 commercially pure cast titanium specimens were randomly subjected to 1 contrast group and 3 test groups, named Ta, Tb and Tc. All test groups were treated with ZrN deposited under different N2 partial pressure by magnetron sputtering (group Ta 1.0x10(-2) Pa, group Tb 5.0x10(-2) Pa and group Tc 10.0x10(-2) Pa). The pure titanium specimens were sintered after surface treatment. The compositions of the deposits were analyzed by X-ray diffraction (XRD). A universal testing machine was used to perform the three-point bending test to evaluate the bonding strength of Ti and porcelain. The microstructure of ZrN, the interface of Ti/porcelain and the fractured Ti surface were observed by scanning electron microscopy (SEM) and digital microscope. The XRD results prove that the ZrN deposits are cubic crystalline phases. The bonding strength of Ti and porcelain of each group are as following: group contrast (26.67 +/- 0.88) MPa, group Ta (49.41 +/- 0.55) MPa, group Tb (54.55 +/- 0.69) MPa and group Tc (46.24 +/- 0.53) MPa. Statistical differences were recorded (P<0.05). The results of SEM show that the Ti/porcelain interface of contrast group possesses pre-cracks, while samples of test group have better combinations. ZrN film deposited by magnetron sputtering can enhance Ti/porcelain bonding. ZrN films deposited under the N-2 partial pressure of 5.0x10(-2) Pa bring the highest Ti/porcelain bonding strength.
引用
收藏
页码:802 / 806
页数:5
相关论文
共 24 条
  • [21] 2-1
  • [22] Low-temperature thermometer using sputtered ZrNx thin film
    Yotsuya, T
    Yoshitake, M
    Kodama, T
    [J]. CRYOGENICS, 1997, 37 (12) : 817 - 822
  • [23] Zhang H, 2006, RARE METAL MAT ENG, V35, P593
  • [24] Zhiguo Z., 2006, Surf. Coat. Technol, V200, P4918