Microstructural Characterization and Cyclic Hot Corrosion Behaviour of Sputtered Co-Al Nanostructured Coatings on Superalloy

被引：9

作者：

Rahman, Atikur ^{[1
,2
]}

Jayaganthan, R. ^{[1
]}

Chandra, Ramesh ^{[2
]}

Ambardar, R. ^{[3
]}

机构：

[1] Indian Inst Technol Roorkee, Dept Met & Mat Engn, Roorkee 247667, Uttar Pradesh, India

[2] Indian Inst Technol Roorkee, Inst Instrumentat Ctr, Roorkee 247667, Uttar Pradesh, India

[3] Natl Inst Technol Hazratbal, Dept Met Engn, Srinagar 190006, Jammu & Kashmir, India

来源：

OXIDATION OF METALS | 2011年 / 76卷 / 3-4期

关键词：

Nanostructured Co-Al coating; Magnetron sputtering; Molten salts; Hot corrosion; HIGH-TEMPERATURE OXIDATION; THERMAL BARRIER COATINGS; BASE SUPERALLOY; ALLOY COATINGS; FUSED NA2SO4; OXIDES; 900-DEGREES-C; ENVIRONMENTS; SOLUBILITIES; SULFIDATION;

D O I：

10.1007/s11085-011-9257-3

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Nanostructured Co-Al coatings on Superni-718 superalloy substrate were deposited by DC/RF magnetron sputtering in the present work. The microstructure and cyclic hot-corrosion behavior of nanostructured Co-Al coatings on Superni-718 superalloy were investigated in molten salt of 40 wt% Na(2)SO(4) + 60 wt% V(2)O(5) at 900 A degrees C. The results showed that a dense scale formed on the coated samples exposed to corrosive environment during thermal cycling. The spinel phases of CoCr(2)O(4), CoAl(2)O(4) and NiCr(2)O(4) were found in the corroded scale of the coatings, resulting in an effective inhibition of O and S diffusion. The sputtered Co-Al coatings exhibited high hot corrosion resistance due to the formation of beta-CoAl phases in the coating. The relevant corrosion mechanisms substantiating the role of coatings are discussed.

引用

页码：307 / 330

页数：24

共 50 条

[41] DRY AND HOT CORROSION BEHAVIOUR OF Al-Ni-Co-x MWCNT COMPOSITES PROCESSED THROUGH POWDER METALLURGY [J].

Padmanaban, M. ;

Thirumurugan, Rama ;

Ramkumar, T. .

SURFACE REVIEW AND LETTERS, 2025, 32 (10)

[42] Hot corrosion behaviour of low Al NiCoCrAlY cladded coatings reinforced by nano-particles on a Ni-base super alloy [J].

Wang, Hongyu ;

Zuo, Dunwen ;

Chen, Gang ;

Sun, Guifang ;

Li, Xiangfeng ;

Cheng, Xu .

CORROSION SCIENCE, 2010, 52 (10) :3561-3567

[43] Hot corrosion Type I of novel Co-based γ/γ′ superalloys with and without Al- and Cr-diffusion coatings [J].

Koenig, Till ;

Hagen, Sebastian P. ;

Virtanen, Sannakaisa ;

Galetz, Mathias C. .

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2024, 75 (12) :1583-1599

[44] Hot corrosion behaviour of double rare-earth oxides co-doped SrZrO3 coatings in molten sulphate-vanadate salt at 900°C [J].

Ma, W. ;

Ren, Y. ;

Bai, Y. ;

Wang, J. ;

Wang, D. ;

Dong, H. .

MATERIALS RESEARCH INNOVATIONS, 2014, 18 :990-996

[45] On the cyclic hot corrosion behaviour of atmospheric plasma sprayed Lanthanum Zirconate based coatings in contact with a mixture of sodium sulphate and vanadate salts: A comparison with the traditional Ysz duplex and NiCrAlY coated samples [J].

Ramachandran, C. S. ;

Balasubramanian, V. ;

Ananthapadmanabhan, P. V. .

VACUUM, 2013, 97 :81-95

[46] Hot corrosion behaviour of plasma sprayed coatings on a Ni-based superalloy in Na2SO4-60%V2O5 environment [J].

Prakash, S ;

Puri, D ;

Singh, H .

ISIJ INTERNATIONAL, 2005, 45 (06) :886-895

[47] Evaluation of hot corrosion behavior of plasma sprayed scandia and yttria co-stabilized nanostructured thermal barrier coatings in the presence of molten sulfate and vanadate salt [J].

Loghman-Estarki, Mohammad Reza ;

Nejati, Mehrdad ;

Edris, Hossein ;

Razavi, Reza Shoja ;

Jamali, Hossein ;

Pakseresht, Amir Hossein .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2015, 35 (02) :693-702

[48] A study on hot corrosion behaviour of Ni-5Al coatings on Ni- and Fe-based superalloys in an aggressive environment at 900 °C [J].

Mahesh, R. A. ;

Jayaganthan, R. ;

Prakash, S. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 460 (1-2) :220-231

[49] Effect of CeO2 on Cyclic Hot-Corrosion Behavior of Detonation-Gun Sprayed Cr3C2-NiCr Coatings on Ni-Based Superalloy [J].

Sekar Saladi ;

Jyoti Menghani ;

Satya Prakash .

Journal of Materials Engineering and Performance, 2015, 24 :1379-1389

[50] Effect of CeO2 on Cyclic Hot-Corrosion Behavior of Detonation-Gun Sprayed Cr3C2-NiCr Coatings on Ni-Based Superalloy [J].

Saladi, Sekar ;

Menghani, Jyoti ;

Prakash, Satya .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (03) :1379-1389

← 1 2 3 4 5 →