Evaluation of temperature and humidity on PV module degradation- in field degradation analysis of crystalline silicon module

被引：0
作者：
Li, Hailing [1 ,2 ,3 ]
Lv, Fang [1 ,2 ]
Diao, Hongwei [1 ,2 ]
Chen, Xu [1 ,2 ]
Wang, Wenjing [1 ,2 ,3 ]
机构：
[1] Chinese Acad Sci, Key Lab Solar Thermal Energy & Photovolta Syst, Beijing 100190, Peoples R China
[2] Chinese Acad Sci, Inst Elect Engn, Beijing, Peoples R China
[3] Univ Chinese Acad Sci UCAS, Beijing 100190, Peoples R China
来源：
2019 IEEE 46TH PHOTOVOLTAIC SPECIALISTS CONFERENCE (PVSC) | 2019年
关键词：
Photovoltaic systems; module; silicon; degradation;
D O I：
10.1109/pvsc40753.2019.8981241
中图分类号：
TE [石油、天然气工业]; TK [能源与动力工程];
学科分类号：
0807 ; 0820 ;
摘要：
PV modules operated in humid and hot climate area in different sites with different operating years were investigated. The average degradation rate is 1.18%/y, higher than guarantee of 20% for 25 years (0.8%/y). By investigating modules from 3 plants operating for 3 years, 6 years and 15 years, the influence of operating year on degradation are studied. As reported before, corrosion of metallic materials is considered to be one of the main degradation models. We find linear relationship between FF and P. degradation, especially at the case with long operating year.
引用
收藏
页码：1986 / 1990
页数：5
相关论文
共 50 条
[41]   Estimation of an Optimal PV Panel Cleaning Strategy Based on Both Annual Radiation Profile and Module Degradation [J].
Alvarez, David L. ;
Al-Sumaiti, Ameena S. ;
Rivera, Sergio R. .
IEEE ACCESS, 2020, 8 (08) :63832-63839
[42]   Correlating Infrared Thermography With Electrical Degradation of PV Modules Inspected in All-India Survey of Photovoltaic Module Reliability 2016 [J].
Chattopadhyay, Shashwata ;
Dubey, Rajiv ;
Bhaduri, Sonali ;
Zachariah, Sachin ;
Singh, Hemant Kumar ;
Solanki, Chetan Singh ;
Kottantharayil, Anil ;
Shiradkar, Narendra ;
Arora, Brij M. ;
Narasimhan, K. L. ;
Vasi, Juzer .
IEEE JOURNAL OF PHOTOVOLTAICS, 2018, 8 (06) :1800-1808
[43]   Identifying PV Module Mismatch Faults by a Thermography-Based Temperature Distribution Analysis [J].
Hu, Yihua ;
Cao, Wenping ;
Ma, Jien ;
Finney, Stephen J. ;
Li, David .
IEEE TRANSACTIONS ON DEVICE AND MATERIALS RELIABILITY, 2014, 14 (04) :951-960
[44]   Thermal recovery effect on light-induced degradation of amorphous silicon solar module under the sunlight [J].
Yamawaki, T ;
Mizukami, S ;
Yamazaki, A ;
Takahashi, H .
SOLAR ENERGY MATERIALS AND SOLAR CELLS, 1997, 47 (1-4) :125-134
[45]   Degradation Analysis of Transient Thermal Characteristics of IGBT Module under Different Working Conditions [J].
Liu X. ;
Li Z. ;
Yao F. .
Diangong Jishu Xuebao/Transactions of China Electrotechnical Society, 2019, 34 :509-517
[46]   Generalized quantitative electroluminescence method for the performance evaluation of defective and unevenly degraded crystalline silicon photovoltaic module [J].
Puranik, Vishal E. ;
Kumar, Ravi ;
Gupta, Rajesh .
PROGRESS IN PHOTOVOLTAICS, 2023, 31 (03) :269-282
[47]   Reassessment of different flat TCO integrated reflectors for the crystalline silicon solar PV module in view of its longer operational life [J].
Agrawal, Monika ;
Chowdhury, Amartya .
PROGRESS IN PHOTOVOLTAICS, 2022, 30 (11) :1325-1342
[48]   Detailed Current Loss Analysis for a PV Module Made With Textured Multicrystalline Silicon Wafer Solar Cells [J].
Peters, Ian Marius ;
Khoo, Yong Sheng ;
Walsh, Timothy Michael .
IEEE JOURNAL OF PHOTOVOLTAICS, 2014, 4 (02) :585-593
[49]   Degradation of plated silicon solar module due to copper diffusion: The role of capping layer formation and contact adhesion [J].
Phua, Benjamin ;
Shen, Xiaowei ;
Hsiao, Pei-Chieh ;
Kong, Charlie ;
Stokes, Alex ;
Lennon, Alison .
SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2020, 215
[50]   Degradation and comparative experimental study of crystalline photovoltaic module after a few years outdoor exposure in casamance and cologne climate [J].
Faye, Issa ;
Ndiaye, Ababacar ;
Kobor, Diouma ;
Philippe, Gabriel Jean ;
Blieske, Ulf ;
Gecke, Rudolph .
2018 7TH INTERNATIONAL ENERGY AND SUSTAINABILITY CONFERENCE (IESC), 2018,
12345