Effect of Cyclic Fatigue Loading on Matrix Multiple Fracture of Fiber-Reinforced Ceramic-Matrix Composites

被引：9

作者：

Li, Longbiao ^{[1
]}

机构：

[1] Nanjing Univ Aeronaut & Astronaut, Coll Civil Aviat, 29 Yudao St, Nanjing 210016, Peoples R China

来源：

CERAMICS-SWITZERLAND | 2019年 / 2卷 / 02期

关键词：

Ceramic-matrix composites (CMCs); Multiple matrix cracking; Cyclic fatigue; Interface debonding; Interface wear; STRESS-STRAIN BEHAVIOR; MULTICRACKING EVOLUTION; TENSILE BEHAVIOR; CRACKING STRESS; DAMAGE; HYSTERESIS; MECHANICS; DESIGN; 2D;

D O I：

10.3390/ceramics2020027

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

In this paper, the effect of cyclic fatigue loading on matrix multiple fracture of fiber-reinforced ceramic-matrix composites (CMCs) is investigated using the critical matrix strain energy (CMSE) criterion. The relationships between multiple matrix cracking, cyclic fatigue peak stress, fiber/matrix interface wear, and debonding are established. The effects of fiber volume fraction, fiber/matrix interface shear stress, and applied cycle number on matrix multiple fracture and fiber/matrix interface debonding and interface wear are discussed. Comparisons of multiple matrix cracking with/without cyclic fatigue loading are analyzed. The experimental matrix cracking of unidirectional SiC/CAS, SiC/SiC, SiC/Borosilicate, and mini-SiC/SiC composites with/without cyclic fatigue loading are predicted.

引用

页码：327 / 346

页数：20

共 50 条

[41] Synergistic effect of arbitrary loading sequence and interface wear on the fatigue hysteresis loops of carbon fiber-reinforced ceramic-matrix composites
Li Longbiao
ENGINEERING FRACTURE MECHANICS, 2015, 146 : 67 - 88
[42] Damage development and lifetime prediction of fiber-reinforced ceramic-matrix composites subjected to cyclic loading at 1300 °C in vacuum, inert and oxidative atmospheres
Li Longbiao
AEROSPACE SCIENCE AND TECHNOLOGY, 2019, 86 : 613 - 629
[43] Micromechanical Modeling Tensile and Fatigue Behavior of Fiber-Reinforced Ceramic-Matrix Composites Considering Matrix Fragmentation and Closure
Li, Longbiao
JOURNAL OF COMPOSITES SCIENCE, 2021, 5 (07):
[44] Synergistic Effects of Temperature and Oxidation on Matrix Cracking in Fiber-Reinforced Ceramic-Matrix Composites
Li Longbiao
Applied Composite Materials, 2017, 24 : 691 - 715
[45] Synergistic Effects of Temperature and Oxidation on Matrix Cracking in Fiber-Reinforced Ceramic-Matrix Composites
Li Longbiao
APPLIED COMPOSITE MATERIALS, 2017, 24 (03) : 691 - 715
[46] Modeling Strength Degradation of Fiber-Reinforced Ceramic-Matrix Composites Subjected to Cyclic Loading at Elevated Temperatures in Oxidative Environments
Li Longbiao
Applied Composite Materials, 2018, 25 : 1 - 19
[47] Relationship Between Hysteresis Dissipated Energy and Temperature Rising in Fiber-Reinforced Ceramic-Matrix Composites Under Cyclic Loading
Li Longbiao
APPLIED COMPOSITE MATERIALS, 2016, 23 (03) : 337 - 355
[48] Time-dependent damage and fracture of fiber-reinforced ceramic-matrix composites at elevated temperatures
Li Longbiao
COMPOSITE INTERFACES, 2019, 26 (11) : 963 - 988
[49] Damage evolution of fiber-reinforced ceramic-matrix composites under stress-rupture and cyclic loading at elevated temperature in oxidizing atmosphere
Li Longbiao
INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2017, 131 : 938 - 955
[50] Modeling Strength Degradation of Fiber-Reinforced Ceramic-Matrix Composites Subjected to Cyclic Loading at Elevated Temperatures in Oxidative Environments
Li Longbiao
APPLIED COMPOSITE MATERIALS, 2018, 25 (01) : 1 - 19

← 1 2 3 4 5 →