Fracture toughness (KIC), hardness, sintering and grain growth behaviour of 8YSCZ/Al2O3 composites produced by colloidal processing

被引:52
作者
Tekeli, S [1 ]
机构
[1] Gazi Univ, Fac Tech Educ, Met Educ Dept, Div Mat, TR-06500 Ankara, Turkey
关键词
cubic zirconia; sinterability; grain growth; fracture toughness; hardness; alumina and colloidal processing;
D O I
10.1016/j.jallcom.2004.08.084
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The influence of Al2O3 content on fracture toughness, hardness, sintering and grain growth behaviour of 8YSCZ/Al2O3 composites were determined using high purity commercial powders of 8 mol% yttria-stabilized cubic zirconia (8YSCZ) doped with 0, 1, 5, 10 wt.% Al2O3. Colloidal processing was used for the mixing of powders in order to achieve a uniform distribution and homogeneous microstructure. The experimental results showed that sintered density increased with Al2O3 content up to 1 wt.% and further increase in Al2O3 content led to a decrease in sintered density. The grain growth in the 0-10 wt.% Al2O3 doped 8YSCZs was studied. The grain growth exponent value and the activation energy for undoped 8YSCZ were found to be 2 and 289 kJ/mol, respectively. The addition of Al2O3 raised the grain growth exponent value to 3 and activation energy for the grain growth process was increased from 289 to 410 kJ/mol for the addition of Al2O3 from 0 to 10 wt.%. The introduction of Al2O3 significantly enhanced the hardness and fracture toughness of 8YSCZ/Al2O3 composites. The hardness and fracture toughness increased with increasing Al2O3 content. The maximum hardness and fracture toughness values reached 1459 kg/mm(2) and 2.41 MPa/m(1/2), respectively with the addition of 10 wt.% Al2O3 while these values were 1314 kg/mm(2) and 1.5MPa/m(1/2) for undoped 8YSCZ. (c) 2004 Elsevier B.V. All rights reserved.
引用
收藏
页码:217 / 224
页数:8
相关论文
共 16 条
[1]   A CRITICAL-EVALUATION OF INDENTATION TECHNIQUES FOR MEASURING FRACTURE-TOUGHNESS .1. DIRECT CRACK MEASUREMENTS [J].
ANSTIS, GR ;
CHANTIKUL, P ;
LAWN, BR ;
MARSHALL, DB .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1981, 64 (09) :533-538
[2]   Microstructure and mechanical properties of yttria stabilized zirconia silicon carbide nanocomposites [J].
Bamba, N ;
Choa, YH ;
Sekino, T ;
Niihara, K .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1998, 18 (06) :693-699
[3]   Microstructural development during final-stage sintering of nanostructured zirconia based ceramics [J].
Betz, U ;
Sturm, A ;
Löffler, JF ;
Wagner, W ;
Wiedenmann, A ;
Hahn, H .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 281 (1-2) :68-74
[4]   PHASE RELATIONS IN ZRO2-MGO SYSTEM [J].
GRAIN, CF .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1967, 50 (06) :288-&
[5]  
KAZUTAKA S, 2001, THESIS TOKYO U
[6]   Synthesis and properties of cubic zirconia-alumina composite by mechanical alloying [J].
Kwon, NH ;
Kim, GH ;
Song, HS ;
Lee, HL .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 299 (1-2) :185-194
[7]  
LEE WE, 1994, CERAMIC MICROSCTRUC
[8]  
Richerson DW, 1992, MODERN CERAMIC ENG P
[9]   PHASE RELATIONSHIPS IN ZIRCONIA-YTTRIA SYSTEM [J].
SCOTT, HG .
JOURNAL OF MATERIALS SCIENCE, 1975, 10 (09) :1527-1535
[10]   Superplastic deformation of cubic zirconia ceramics with intergranular phases [J].
Sharif, AA ;
Imamura, PH ;
Mecartney, ML .
TOWARDS INNOVATION IN SUPERPLASTICITY II, 1999, 304-3 :443-450