Heteroepitaxial growth of tungsten oxide films on silicon(100) using a BaF2 buffer layer

被引:12
作者
Doucette, LD [1 ]
Santiago, F
Moran, SL
Lad, RJ
机构
[1] Univ Maine, Surface Sci & Technol Lab, Orono, ME 04469 USA
[2] USN, Ctr Surface Warfare, Dahlgren Div, Dahlgren, VA 22448 USA
[3] Univ Maine, Surface Sci & Technol Lab, Orono, ME 04469 USA
关键词
D O I
10.1557/JMR.2003.0399
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Multidomained heteroepitaxial WO, films were grown on Si(100) substrates using a (111)-oriented BaF2 buffer layer at the WO3-Si interface. The 30-nm-thick BaF2 layer, grown by very low rate molecular-beam epitaxy, consisted of four equivalent crystalline domains oriented about the BaF2[111] axis, which provided templates for heteroepitaxial WO3 film growth. The WO3 films were grown by electron cyclotron resonance oxygen plasma-assisted electron beam evaporation of a WO3 source, and the temperature range was varied between 25 degreesC and 600 degreesC. At an optimal deposition temperature of approximately 450 degreesC, monoclinic-phase WO3 films were produced, which consisted of coexisting (002), (020), and (200) in-plane orientations with respect to the BaF,(111)/Si(100) substrate. During growth, an interfacial barium tungstate (BaWO4) reaction product formed at the WO3-BaF2 interface. The{112} planes of this BaWO4 layer also have a multidomained heteroepitaxial orientation with respect to the BaF2(111) buffer layer. Postdeposition annealing experiments in air for 24 h at 400 degreesC indicated that the heteroepitaxial BaWO4 and WO3 layers remain stable. A thermodynamic argument is used to explain the BaWO4 interfacial reaction during initial growth stages, and kinetically limited diffusion processes through the BaWO4 layer coupled with lattice matching across the WO3-BaWO4 interface are proposed to be responsible for the formation of stable WO3 films at later growth stages.
引用
收藏
页码:2859 / 2868
页数:10
相关论文
共 34 条
[1]   EFFECT OF HEAT-TREATMENT ON THE STRUCTURE, COMPOSITION AND ELECTROCHROMIC PROPERTIES OF EVAPORATED TUNGSTEN-OXIDE FILMS .1. [J].
AGRAWAL, A ;
HABIBI, H .
THIN SOLID FILMS, 1989, 169 (02) :257-270
[2]   Ammonia gas sensor using thick film of Au-loaded tungsten trioxide [J].
Ando, M ;
Tsuchida, T ;
Suto, S ;
Suzuki, T ;
Nakayama, C ;
Miura, N ;
Yamazoe, N .
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1996, 104 (12) :1112-1116
[3]  
[Anonymous], 1999, TUNGSTEN PROPERTIES, DOI DOI 10.1007/978-1-4615-4907-9
[4]   MICROSTRUCTURAL EFFECTS IN WO3 GAS-SENSING FILMS [J].
ANTONIK, MD ;
SCHNEIDER, JE ;
WITTMAN, EL ;
SNOW, K ;
VETELINO, JF .
THIN SOLID FILMS, 1995, 256 (1-2) :247-252
[5]  
Barin I., 2008, Thermochemical Data of Pure Substances, VThird
[6]   THE MECHANISM OF OPERATION OF WO3-BASED H2S SENSORS [J].
BARRETT, EPS ;
GEORGIADES, GC ;
SERMON, PA .
SENSORS AND ACTUATORS B-CHEMICAL, 1990, 1 (1-6) :116-120
[7]   Epitaxial growth and properties of thin film oxides [J].
Chambers, SA .
SURFACE SCIENCE REPORTS, 2000, 39 (5-6) :105-180
[8]  
Chase M.W., 1998, NIST JANAF THEMOCHEM, V4th, P1
[9]  
CHU TK, 1994, MATER RES SOC SYMP P, V334, P501
[10]   OPTICAL AND PHOTOELECTRIC PROPERTIES AND COLOR CENTERS IN THIN-FILMS OF TUNGSTEN OXIDE [J].
DEB, SK .
PHILOSOPHICAL MAGAZINE, 1973, 27 (04) :801-822