Synthesis and properties of trifluoromethyl groups containing epoxy resins cured with amine for low Dk materials

被引：13

作者：

Wang, J. Y. ^{[1
]}

Yang, S. Y. ^{[1
]}

Huang, Y. L. ^{[1
]}

Tien, H. W. ^{[1
]}

Chin, W. K. ^{[1
]}

Ma, C. C. M. ^{[1
]}

Shu, W. J. ^{[2
]}

机构：

[1] Natl Tsing Hua Univ, Dept Chem Engn, Hsinchu, Taiwan

[2] Ta Hwa Inst Technol, Dept Chem & Mat Engn, Chiunglin, Taiwan

来源：

JOURNAL OF APPLIED POLYMER SCIENCE | 2012年 / 124卷 / 03期

关键词：

epoxy resins; thermal behaviors; dielectric constants; free volume; LOW DIELECTRIC-CONSTANT; THERMOGRAVIMETRIC ANALYSIS; PERFLUOROBUTENYLOXY GROUP; POLYMERS; BEHAVIOR; MICROELECTRONICS; SOLVENT; CHAIN;

D O I：

10.1002/app.35300

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

The study synthesized a trifluoromethyl (CF3) groups with a modified epoxy resin, diglycidyl ether of bisphenol F (DGEBF), using environmental friendly methods. The epoxy resin was cured with 4,4'-diaminodiphenyl-methane (DDM). For comparison, this study also investigated curing of commercially available diglycidyl ether of bisphenol A (DGEBA) with the same curing agent by varying the ratios of DGEBF. The structure and physical properties of the epoxy resins were characterized to investigate the effect of injecting fluorinated groups into epoxy resin structures. Regarding the thermal behaviors of the specimens, the glass transition temperatures (Tg) of 50-160 degrees C and the thermal decomposition temperatures of 200-350 degrees C at 5% weight loss (Td5%) in nitrogen decreased as amount of DGEBF increased. The different ratios of cured epoxy resins showed reduced dielectric constants (Dk) (2.033.80 at 1 MHz) that were lower than those of pure DGEBA epoxy resins. Reduced dielectric constant is related to high electrronegativity and large free volume of fluorine atoms. In the presence of hydrophobic CF3 groups, the epoxy resins exhibited low moisture absorption and higher contact angles. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012

引用

页码：2615 / 2624

页数：10

共 48 条

[1]

Castelvetro V, 2001, J POLYM SCI POL CHEM, V39, P32, DOI 10.1002/1099-0518(20010101)39:1<32::AID-POLA40>3.0.CO

[2]

2-5

[3]

Charrier J. M., 2000, POLYM MAT PROCESSING

[4] EFFECT OF THE EXTENT OF CURE ON THE MODULUS, GLASS-TRANSITION, WATER-ABSORPTION, AND DENSITY OF AN AMINE-CURED EPOXY [J].