The formation mechanism of characteristic region at crack initiation for very-high-cycle fatigue of high-strength steels

被引:233
作者
Hong, Youshi [1 ]
Liu, Xiaolong [1 ]
Lei, Zhengqiang [1 ]
Sun, Chengqi [1 ]
机构
[1] Chinese Acad Sci, Inst Mech, LNM, Beijing 100190, Peoples R China
基金
中国国家自然科学基金;
关键词
Very-high-cycle fatigue; Fatigue crack initiation; Fine-granular-area; Nanograins; High-strength steels; CHROMIUM-BEARING STEEL; LONG-LIFE FATIGUE; N-GREATER-THAN-10(7) CYCLES; RESIDUAL-STRESSES; BEHAVIOR; PROPAGATION; INCLUSIONS; DAMAGE; SIZE; LOCATION;
D O I
10.1016/j.ijfatigue.2015.11.029
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
For high-strength steels, the crack initiation of very-high-cycle fatigue (VHCF) is commonly at the interior of material with fish-eye (FiE) morphology containing a fine-granular-area (FGA) surrounding an inclusion as crack origin, and FGA is regarded as the characteristic region of crack initiation. Here, we carefully examined the micro-morphology of FGA and FiE for two high-strength steels. The results revealed that the microscopic nature of FGA is a thin layer of nanograins. Then we proposed the formation mechanism of FGA: Numerous Cyclic Pressing (NCP) between originated crack surfaces, which causes grain refinement at originated crack wake and therefore the formation of FGA. The results of second set experiment showed that the cases with negative stress ratios exhibit the prevalence of nanograin layer in FGA region and the nanograin layer vanishes for the cases with positive stress ratios, which is a verification of the proposed NCP model. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码:108 / 118
页数:11
相关论文
共 40 条
[1]   Effects of residual stresses on fracture behaviour-experimental results and assessment methods [J].
Ainsworth, RA ;
Sharples, JK ;
Smith, SD .
JOURNAL OF STRAIN ANALYSIS FOR ENGINEERING DESIGN, 2000, 35 (04) :307-316
[2]   Transient behaviour in the numerical analysis of plasticity induced crack closure [J].
Antunes, F. V. ;
Marques, G. A. S. ;
Chegini, A. G. ;
Correia, L. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2014, 37 (05) :526-538
[3]  
Bathias Claude, 2005, MECH ENG SE
[4]   Fatigue strength of severely notched specimens made of Ti-6Al-4V under multiaxial loading [J].
Berto, F. ;
Campagnolo, A. ;
Lazzarin, P. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2015, 38 (05) :503-517
[5]   Formation of fine grained area in martensitic steel during very high cycle fatigue [J].
Chai, G. ;
Forsman, T. ;
Gustavsson, F. ;
Wang, C. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2015, 38 (11) :1315-1323
[6]   Study of crack initiation or damage in very high cycle fatigue using ultrasonic fatigue test and microstructure analysis [J].
Chai, Guocai ;
Zhou, Nian .
ULTRASONICS, 2013, 53 (08) :1406-1411
[7]  
Elber W., 1970, Engineering Fracture Mechanics, V2, P37, DOI 10.1016/0013-7944(70)90028-7
[8]   Extreme grain refinement by severe plastic deformation: A wealth of challenging science [J].
Estrin, Y. ;
Vinogradov, A. .
ACTA MATERIALIA, 2013, 61 (03) :782-817
[9]   Effect of residual stresses on crack behaviour in single edge bending specimens [J].
Farahani, M. ;
Sattari-Far, I. ;
Akbari, D. ;
Alderliesten, R. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2013, 36 (02) :115-126
[10]   Variable amplitude loading of spray-formed hypereutectic aluminium silicon alloy DISPAL® S232 in the VHCF regime [J].
Fitzka, M. ;
Mayer, H. ;
Schuller, R. ;
Stanzl-Tschegg, S. E. ;
Przeorski, T. ;
Krug, P. .
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2014, 37 (09) :945-957