Preparation and characterisation of low-friction TiB2-based coatings by incorporation of C or MoS2

被引：81

作者：

Gilmore, R ^{[1
]}

Baker, MA ^{[1
]}

Gibson, PN ^{[1
]}

Gissler, W ^{[1
]}

机构：

[1] Commiss European Communities, Joint Res Ctr, Inst Adv Mat, I-21020 Ispra, Va, Italy

来源：

SURFACE & COATINGS TECHNOLOGY | 1998年 / 105卷 / 1-2期

关键词：

hard coatings; low friction; TiB2-C; TiB2-MoS2;

D O I：

10.1016/S0257-8972(98)00445-9

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Hard, low-friction, TiB2-based coatings incorporating C or MoS2 have been synthesised by magnetron co-sputtering from TIB2 and C or MoS2 targets. The coating microstructure was characterised by glancing angle X-ray diffractometry and photoelectron spectroscopy. The friction coefficient was measured using pin-ore-disk tribometry and hardness by nanoindentation. Our TiB2-C coatings were found to consist of two phases, diamond-like carbon (DLC) and a hexagonal TiB2 type structure into which carbon is incorporated. A friction-reducing effect was observed only at C concentrations above 66%, where a significant quantity of DLC phase was able to form. For TiB2-MoS2 coatings, a reduced friction was observed, even at low concentrations of MoS2. With both types of lubricants, a trade-off between hardness and friction coefficient was found. Coatings exhibiting a relatively high hardness of 20 GPa and friction coefficients as low as 0.05 could be obtained by choosing a suitable composition. Low friction could be obtained for temperatures as high as 400 degrees C for the TiB2-MoS2 coatings, whilst the TiB2-C coatings exhibited a sharp increase in friction coefficient above 150 degrees C. (C) 1998 Elsevier Science S.A.

引用

页码：45 / 50

页数：6

共 11 条

[1] PREPARATION AND PROPERTIES OF DIFFERENT TYPES OF SPUTTERED MOS2 FILMS [J].

BUCK, V .

WEAR, 1987, 114 (03) :263-274

[2] Today's applications and future developments of coatings for drills and rotating cutting tools [J].

Cselle, T ;

Barimani, A .

SURFACE & COATINGS TECHNOLOGY, 1995, 76-77 (1-3) :712-718

[3]

DOERNER MF, 1992, J MATER RES, V1, P397

[4] Advanced solid lubricant coatings for high vacuum environments [J].

Donnet, C .

SURFACE & COATINGS TECHNOLOGY, 1996, 80 (1-2) :151-156

[5] Present progress in the development of low friction coatings [J].

Hirvonen, JP ;

Koskinen, J ;

Jervis, JR ;

Nastasi, M .

SURFACE & COATINGS TECHNOLOGY, 1996, 80 (1-2) :139-150

[6]

*INT CTR DIFFR DAT, 1972, POWD DIFFR FIL

[7]

LANCASTER JK, 1975, ASLE TRANS, V18, P187, DOI 10.1080/05698197508982761

[8] An investigation of the relationship between graphitization and frictional behavior of DLC coatings [J].

Liu, Y ;

Erdemir, A ;

Meletis, EI .

SURFACE & COATINGS TECHNOLOGY, 1996, 86-7 (1-3) :564-568

[9] Tribological behaviour of homogeneous Ti-B-N, Ti-B-N-C and TiN/h-BN/TiB2 multilayer coatings [J].

Mollart, TP ;

Haupt, J ;

Gilmore, R ;

Gissler, W .

SURFACE & COATINGS TECHNOLOGY, 1996, 86 (1-3) :231-236

[10]

Pauleau Y., 1995, NATO ASI SERIES E, V290, P475

← 1 2 →