Microstructural evolution and mechanical properties of Ti-5Al-5Mo-5V-3Cr alloy by heat treatment with continuous temperature gradient

被引:18
作者
Xu, Sheng-hang [1 ]
Liu, Yong [1 ]
Liu, Bin [1 ]
Wang, Xin [1 ]
Chen, Zhi-xing [1 ]
机构
[1] Cent S Univ, State Key Lab Powder Met, Changsha 410083, Hunan, Peoples R China
关键词
Ti-5Al-5Mo-5V-3Cr alloy; high throughput method; pseudo-spinodal decomposition; temperature gradient; microstructure; mechanical properties; TI-5AL-5V-5MO-3CR ALLOY; PHASE-TRANSFORMATIONS; OMEGA PRECIPITATION; COOLING RATE; TI ALLOY; BETA; BEHAVIOR; DECOMPOSITION; NUCLEATION; GROWTH;
D O I
10.1016/S1003-6326(18)64660-6
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
A new high throughput heat-treatment method with a continuous temperature gradient between 600 and 700 degrees C was utilized on the Ti-5553 alloy (Ti-5Al-5Mo-5V-3Cr, mass fraction, %). The temperature gradient was induced by the variation of the axial section of sample, which was heated by the direct current. The variation of continuous cooling rates on the treated sample was realized by using the end quenching method. The microstructural evolution and mechanical properties under different heat treatment conditions were evaluated. The results show that the pseudo-spinodal decomposition of the alloy occurs at (617 +/- 1) degrees C, and the size of the precipitated alpha phase is around 300 nm. Moreover, the highest microhardness is obtained after the heat treatment at the pseudo-spinodal decomposition temperature for 4 h. These indicate that the high throughput method is efficient and fast to determine the phase transformation temperature and corresponding microstructural evolution of alloys.
引用
收藏
页码:273 / 281
页数:9
相关论文
共 30 条
[1]   Influence of cooling rate on microstructure of Ti-Nb alloy for orthopedic implants [J].
Afonso, C. R. M. ;
Aleixo, G. T. ;
Ramirez, A. J. ;
Caram, R. .
MATERIALS SCIENCE & ENGINEERING C-BIOMIMETIC AND SUPRAMOLECULAR SYSTEMS, 2007, 27 (04) :908-913
[2]   PHASE-TRANSFORMATIONS IN THE (TI,NB)3AL SECTION OF THE TI-AL-NB SYSTEM .2. EXPERIMENTAL TEM STUDY OF MICROSTRUCTURES [J].
BENDERSKY, LA ;
BOETTINGER, WJ .
ACTA METALLURGICA ET MATERIALIA, 1994, 42 (07) :2337-2352
[3]   Pseudospinodal mechanism for fine α/β microstructures in β-Ti alloys [J].
Boyne, A. ;
Wang, D. ;
Shi, R. P. ;
Zheng, Y. ;
Behera, A. ;
Nag, S. ;
Tiley, J. S. ;
Fraser, H. L. ;
Banerjee, R. ;
Wang, Y. .
ACTA MATERIALIA, 2014, 64 :188-197
[4]   Influence of cooling rate on the precipitation behavior in Ti-Nb-Mo microalloyed steels during continuous cooling and relationship to strength [J].
Bu, F. Z. ;
Wang, X. M. ;
Chen, L. ;
Yang, S. W. ;
Shang, C. J. ;
Misra, R. D. K. .
MATERIALS CHARACTERIZATION, 2015, 102 :146-155
[5]   The Dependence of Isothermal ω Precipitation on the Quenching Rate in a Metastable β-Ti Alloy [J].
Chen, Jing ;
Xiao, Wenlong ;
Dargusch, Matthew Simon ;
Ma, Chaoli .
SCIENTIFIC REPORTS, 2015, 5
[6]   Development of α-phase morphologies during low temperature isothermal heat treatment of a Ti-5Al-5Mo-5V-3Cr alloy [J].
Dehghan-Manshadi, Ali ;
Dippenaar, Rian J. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (03) :1833-1839
[7]   Experimental evidence of concurrent compositional and structural instabilities leading to ω precipitation in titanium-molybdenum alloys [J].
Devaraj, A. ;
Nag, S. ;
Srinivasan, R. ;
Williams, R. E. A. ;
Banerjee, S. ;
Banerjee, R. ;
Fraser, H. L. .
ACTA MATERIALIA, 2012, 60 (02) :596-609
[8]   The interrelationship of fracture toughness and microstructure in a new near β titanium alloy Ti-7Mo-3Nb-3Cr-3Al [J].
Fan, J. K. ;
Li, J. S. ;
Kou, H. C. ;
Hua, K. ;
Tang, B. .
MATERIALS CHARACTERIZATION, 2014, 96 :93-99
[9]   Nano-chessboard superlattices formed by spontaneous phase separation in oxides [J].
Guiton, Beth S. ;
Davies, Peter K. .
NATURE MATERIALS, 2007, 6 (08) :586-591
[10]   Cyclic Deformation Response of β-Annealed Ti-5Al-5V-5Mo-3Cr Alloy Under Compressive Loading Conditions [J].
Huang, Jun ;
Wang, Zhirui ;
Zhou, Jie .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2011, 42A (09) :2868-2880