Preparation of textured porous Al2O3 ceramics by slip casting in a strong magnetic field and its mechanical properties

被引：33

作者：

Yang, Zhigang ^{[1
]}

Yu, Jianbo ^{[1
]}

Li, Chuanjun ^{[1
]}

Zhong, Yunbo ^{[1
]}

Xuan, Weidong ^{[1
]}

Ren, Zhongming ^{[1
]}

Wang, Qiuliang ^{[2
]}

Dai, Yinming ^{[2
]}

Wang, Hui ^{[2
]}

机构：

[1] Shanghai Univ, Key Lab Modern Met & Mat Preparat, Shanghai 200072, Peoples R China

[2] Chinese Acad Sci, Inst Elect Engn, Beijing 100190, Peoples R China

来源：

CRYSTAL RESEARCH AND TECHNOLOGY | 2015年 / 50卷 / 08期

关键词：

porous Al2O3; texture; strong magnetic field; the bending strength; SINTERING SHRINKAGE; ALUMINA; FABRICATION; ORIENTATION; PARTICLES; GELATION; GROWTH; PORES;

D O I：

10.1002/crat.201500080

中图分类号：

O7 [晶体学];

学科分类号：

0702 ; 070205 ; 0703 ; 080501 ;

摘要：

The textured porous Al2O3 ceramics were prepared by slip casting in a strong magnetic field of 6 T and subsequently sintering. The c axis of Al2O3 grain was oriented parallel to the direction of the magnetic field and the textured porous microstructure with plate-shape grains was formed. The porosity of textured porous Al2O3 ceramic was 30.37% and the relative density reached 66.29% when the sintering temperature is 1600 degrees C. The textured porous Al2O3 green body showed the linear shrinkage anisotropy. The bending strength of the textured porous Al2O3 ceramics depended on the alignment direction of plate-shape grains.

引用

页码：645 / 653

页数：9

共 22 条

[1] The orientation mechanism of (Ca,Sr)Bi4Ti4O15 ceramics prepared by slip casting in high magnetic field and subsequent sintering [J].

Cao, Ziping ;

Sassa, Kensuke ;

Asai, Shigeo .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2007, 27 (07) :2591-2596

[2] Freeze-casting of porous ceramics: A review of current achievements and issues [J].

Deville, Sylvain .

ADVANCED ENGINEERING MATERIALS, 2008, 10 (03) :155-169

[3] Fabrication and properties of ultra highly porous silicon carbide by the gelation-freezing method [J].

Fukushima, Manabu ;

Nakata, Masayuki ;

Zhou, You ;

Ohji, Tatsuki ;

Yoshizawa, Yu-ichi .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2010, 30 (14) :2889-2896

[4] Fabrication of porous ceramics with controlled pore size by colloidal processing [J].

Sakka, Y ;

Tang, FQ ;

Fudouzi, H ;

Uchikoshi, T .

SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2005, 6 (08) :915-920

[5] Textured development of feeble magnetic ceramics by colloidal processing under high magnetic field [J].

Sakka, Y ;

Suzuki, TS .

JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2005, 113 (1313) :26-36

[6] Fabrication and some properties of textured alumina-related compounds by colloidal processing in high-magnetic field and sintering [J].

Sakka, Yoshio ;

Suzuki, Tohru S. ;

Uchikoshi, Tetsuo .

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2008, 28 (05) :935-942

[7] Anisotropic sintering shrinkage of spherical alumina particle compact aligned in high magnetic field [J].

Shui, A ;

Zeng, LK ;

Liu, PG ;

Cheng, XS ;

Uematsu, K .

JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2006, 114 (1327) :290-292

[8] Relationship between sintering shrinkage anisotropy and particle orientation for alumina powder compacts [J].

Shui, Anze ;

Zeng, Lingke ;

Uematsu, Keizo .

SCRIPTA MATERIALIA, 2006, 55 (09) :831-834

[9] Stability of dispersions of colloidal alumina particles in aqueous suspensions [J].

Singh, BP ;

Menchavez, R ;

Takai, C ;

Fuji, M ;

Takahashi, M .

JOURNAL OF COLLOID AND INTERFACE SCIENCE, 2005, 291 (01) :181-186

[10] ORIGIN AND GROWTH-KINETICS OF PLATELIKE ABNORMAL GRAINS IN LIQUID-PHASE-SINTERED ALUMINA [J].

SONG, H ;

COBLE, RL .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1990, 73 (07) :2077-2085

← 1 2 3 →