An EBSD local texture study on the nucleation of recrystallization at shear bands in the alloy Al-3Mg

被引：67

作者：

Engler, O ^{[1
]}

机构：

[1] Univ Calif Los Alamos Natl Lab, Div Mat Sci & Technol MST 8, Los Alamos, NM 87545 USA

来源：

SCRIPTA MATERIALIA | 2001年 / 44卷 / 02期

关键词：

recrystallization and recovery; nucleation and growth; aluminum; texture; microstructure;

D O I：

10.1016/S1359-6462(00)00597-2

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The nucleation of recrystallization at shear bands in the Al-3%Mg is studied using electron back-scatter diffraction (EBSD) local texture measurements. AlMg alloys are prone to shear banding. The recrystallization textures intensities of the Goss and Q orientations are described. These orientations nucleate in the shear bands as measured.

引用

页码：229 / 236

页数：8

共 20 条

[1]

[Anonymous], MAT SCI FORUM

[2] THE ITERATIVE SERIES-EXPANSION METHOD FOR QUANTITATIVE TEXTURE ANALYSIS .1. GENERAL OUTLINE [J].

DAHMS, M ;

BUNGE, HJ .

JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1989, 22 :439-447

[3]

DUCKHAM A, UNPUB ACTA MAT

[4]

ENGLER O, 1995, ACTA METALL MATER, V43, P121, DOI 10.1016/0956-7151(94)00226-8

[5] On the origin of the R orientation in the recrystallization textures of aluminum alloys [J].

Engler, O .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (06) :1517-1527

[6]

Engler O, 1996, MATER SCI TECH SER, V12, P859, DOI 10.1179/026708396790122206

[7]

ENGLER O, 1995, TEXTURE MICROSTRUCT, V23, P61, DOI DOI 10.1155/TSM.23.61

[8]

GODFREY A, 1995, P 16 RISO INT S ROSK, P365

[9] OVERVIEW NO 93 - ON THE ORIGIN OF RECRYSTALLIZATION TEXTURES IN ALUMINUM [J].

HJELEN, J ;

ORSUND, R ;

NES, E .

ACTA METALLURGICA ET MATERIALIA, 1991, 39 (07) :1377-1404

[10]

JASIENSKI Z, 1996, P ICOTOM, V11, P484

← 1 2 →