Influences of the microstructure on the wear resistance of cobalt-based alloy coatings obtained by plasma transferred arc process

被引:0
作者
Hou, QY [1 ]
Gao, JS [1 ]
机构
[1] Anhui Univ Technol, Sch Mat Sci & Engn, Maanshan 243002, Peoples R China
关键词
cobalt-based alloy; plasma transferred arc (PTA); microstructure; wear;
D O I
暂无
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The microstructure, substructure, and wear characteristic of cobalt-based alloy coatings obtained by plasma transferred arc (PTA) process were investigated using optical metallurgical microscope, X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), and dry sand abrasion tester (DSAT). The aging effect on the structure and wear resistance of the cobalt-based PTA coating was also studied. The results show that the as-welded coating consists of cobalt-based solid solution with face-centered cubic structure and hexagonal (CrFe)(7)C-3. There are a lot of stacking faults existing in the cobalt-based solid solution. After aging at 600 degrees C for 60 h, the microstructure becomes coarse, and another carbide (CrFe)(23)C-6 precipitates. As a result, the wear mass loss of the aged sample is higher than that of the as-welded sample.
引用
收藏
页码:76 / 81
页数:6
相关论文
共 17 条
[1]   Formation of WC-Co layers by an electron beam cladding method and evaluation of the layer properties [J].
Abe, N ;
Morimoto, J ;
Tomie, M ;
Doi, C .
VACUUM, 2000, 59 (01) :373-380
[2]   On the wear behavior of surface clad layers under high temperature [J].
Aoh, JN ;
Jeng, YR ;
Chu, EL ;
Wu, LT .
WEAR, 1999, 225 :1114-1122
[3]   On the wear characteristics of cobalt-based hardfacing layer after thermal fatigue and oxidation [J].
Aoh, JN ;
Chen, JC .
WEAR, 2001, 250 (PART 1) :611-620
[4]   A study on the surface treatment of "Calmax" tool steel by a plasma transferred arc (PTA) process [J].
Bourithis, E ;
Tazedakis, A ;
Papadimitriou, G .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2002, 128 (1-3) :169-177
[5]  
CHAN WS, 1999, MAT T JIM, V37, P50
[6]   TEM characterization of plasma-sprayed thermal barrier coatings and ceramic-metal interfaces after hot isostatic pressing [J].
Chen, HC ;
Heberlein, J ;
Pfender, E .
THIN SOLID FILMS, 1997, 301 (1-2) :105-114
[7]  
CHEN HC, 1991, ACTA METALLURIGCA SI, V2, pA115
[8]   Fitting corrosion of 304 stainless steel after laser surface melting in argon and nitrogen atmospheres [J].
Conde, A ;
García, I ;
de Damborenea, JJ .
CORROSION SCIENCE, 2001, 43 (05) :817-828
[9]   Metal-matrix composite coatings by PTA surfacing [J].
Deuis, RL ;
Yellup, JM ;
Subramanian, C .
COMPOSITES SCIENCE AND TECHNOLOGY, 1998, 58 (02) :299-309
[10]   Vapour deposited Zn-Cr Alloy coatings for enhanced manufacturing and corrosion resistance of steel sheets [J].
Guzman, L ;
Adami, M ;
Gissler, W ;
Klose, S ;
De Rossi, S .
SURFACE & COATINGS TECHNOLOGY, 2000, 125 (1-3) :218-222