Corrosion measurement on shear strength of Cu/Sn-9Zn/Cu lap joints

被引：4
作者：
Affendy, Muhammad Ghaddafy [1 ]
Yahaya, Muhamad Zamri [1 ]
Ani, Fakhrozi Che [2 ]
Mohamad, Ahmad Azmin [1 ]
机构：
[1] Univ Sains Malaysia, Sch Mat & Mineral Resources Engn, Nibong Tebal 14300, Penang, Malaysia
[2] Jabil Circuit Sdn Bhd, Bayan Lepas 11900, Penang, Malaysia
来源：
MEASUREMENT | 2015年 / 66卷
关键词：
Corrosion; Shear strength; Lap joints; NaCl; Morphology; LEAD-FREE SOLDERS; SN-ZN SOLDERS; MECHANICAL-PROPERTIES; TENSILE PROPERTIES; ADHESION STRENGTH; MICROSTRUCTURE; CU; AG; BEHAVIOR; AL;
D O I：
10.1016/j.measurement.2015.02.016
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Corrosion of the Cu/Sn-9Zn/Cu lap joints in 3.5 wt.% NaCl solution showed reduction in the ultimate shear strength with increasing immersion time. The highest ultimate shear strength value obtained was at 122.67 MPa before immersion while the lowest value was 85.32 MPa after immersion for 28 days. Corrosion products consist of tin (II) chloride and zinc hydroxide chloride had been obtained due to the active dissolution of tin. The formation of pits observed on the lap joints marked as stress concentration points which are detrimental toward the shear strength. Upon longer immersion period, the pit coalescence and propagation led to the existence of long, deep cracks. The fracture paths nucleates from the cracks clearly established the mechanism of the fracture formation for the Cu/Sn- 9Zn/Cu lap joints. The fracture analysis together with the presence of the corrosion by-products fully reiterated that corrosion activities was the main factor for the decrease in shear strength of Cu/Sn- 9Zn/Cu lap joints. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：195 / 203
页数：9
相关论文
共 50 条
  • [1] Affendy M., 2003, J KING SAUD U ENG SC
  • [2] Affendy M.G., 2014, INT J ELECTROACT MAT, V2, P8
  • [3] Affendy MG, 2012, INT J ELECTROCHEM SC, V7, P4951
  • [4] Influence of Ag micro-particle additions on the microstructure, hardness and tensile properties of Sn-9Zn binary eutectic solder alloy
    Ahmed, Mansur
    Fouzder, Tama
    Sharif, A.
    Gain, Asit Kumar
    Chan, Y. C.
    [J]. MICROELECTRONICS RELIABILITY, 2010, 50 (08) : 1134 - 1141
  • [5] Effect of bismuth and silver on the corrosion behavior of Sn-9Zn alloy in NaCl 3 wt.% solution
    Ahmido, A.
    Sabbar, A.
    Zouihri, H.
    Dakhsi, K.
    Guedira, F.
    Serghini-Idrissi, M.
    El Hajjaji, S.
    [J]. MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2011, 176 (13): : 1032 - 1036
  • [6] Development of high strength Sn-Cu solder using copper particles at nanolength scale
    Alam, M. E.
    Nai, S. M. L.
    Gupta, M.
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 476 (1-2) : 199 - 206
  • [7] Pitting corrosion of zinc in neutral halide solutions
    Assaf, FH
    Abd El-Rehiem, SS
    Zaky, AM
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 1999, 58 (01) : 58 - 63
  • [8] Microstructure and adhesion strength of Sn-9Zn-xAg lead-free solders wetted on Cu substrate
    Chang, Tao-Chih
    Chou, Shih-Min
    Hon, Min-Hsiung
    Wang, Moo-Chin
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 429 (1-2): : 36 - 42
  • [9] Recent advances on kinetic analysis of electromigration enhanced intermetallic growth and damage formation in Pb-free solder joints
    Chao, Brook Huang-Lin
    Zhang, Xuefeng
    Chae, Seung-Hyun
    Ho, Paul S.
    [J]. MICROELECTRONICS RELIABILITY, 2009, 49 (03) : 253 - 263
  • [10] Effects of small additions of Ag, Al, and Ga on the structure and properties of the Sn-9Zn eutectic alloy
    Chen, KI
    Cheng, SC
    Wu, S
    Lin, KL
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2006, 416 (1-2) : 98 - 105
12345