Heavily doped polycrystalline 3C-SiC growth on SiO2/Si(100) substrates for resonator applications

被引:4
作者
Sun, Guosheng [1 ]
Ning, Jin [1 ]
Liu, Xingfang [1 ]
Zhao, Yongmei [1 ]
Li, Jiaye [1 ]
Wang, Lei [1 ]
Zhao, Wanshun [1 ]
Wang, Liang [1 ]
机构
[1] Chinese Acad Sci, Inst Semicond, Beijing 100083, Peoples R China
来源
SILICON CARBIDE AND RELATED MATERIALS 2006 | 2007年 / 556-557卷
关键词
polycrystalline; 3C-SiC; resonator; doping;
D O I
10.4028/www.scientific.net/MSF.556-557.179
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
3C-SiC is a promising material for the development of microelectromechanical systems (MEMS) applications in harsh environments. This paper presents the LPCVD growth of heavily nitrogen doped polycrystalline 3C-SiC films on Si wafers with 2.0 mu m-thick silicon dioxide (SiO2) films for resonator applications. The growth has been performed via chemical vapor deposition using SiH4 and C2H4 precursor gases with carrier gas of H-2 in a newly developed vertical CVD chamber. NH3 was used as n-type dopant. 3C-SiC films were characterized by scanning electron microscopy (SEM), x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS), secondary ion mass spectroscopy (SIMS), and room temperature Hall Effect measurements. It was shown that there is no voids at the interface between 3C-SiC and SiO2. Undoped 3C-SiC films show n-type conduction with resisitivity, Hall mobility, and carrier concentration at room temperature of about 0.56 Omega center dot cm, 54 cm(2)/Vs, and 2.0x 10(17) cm(-3), respectively. The heavily nitrogen doped polycrystalline 3C-SiC with the resisitivity of less than 10(-3) Omega center dot cm was obtained by in-situ doping. Polycrystalline SiC resonators have been fabricated preliminarily on these heavily doped SiC films with thickness of about 2 mu m. Resonant frequency of 49.1 KHz was obtained under atmospheric pressure.
引用
收藏
页码:179 / 182
页数:4
相关论文
共 8 条
[1]   A high temperature pressure sensor prepared by selective deposition of cubic silicon carbide on SOI substrates [J].
Eickhoff, M ;
Möller, H ;
Kroetz, G ;
Berg, JV ;
Ziermann, R .
SENSORS AND ACTUATORS A-PHYSICAL, 1999, 74 (1-3) :56-59
[2]   Fracture of polycrystalline 3C-SiC films in microelectromechanical systems [J].
Gao, D ;
Carraro, C ;
Radmilovic, V ;
Howe, RT ;
Maboudian, R .
JOURNAL OF MICROELECTROMECHANICAL SYSTEMS, 2004, 13 (06) :972-976
[3]   PRODUCTION OF LARGE-AREA SINGLE-CRYSTAL WAFERS OF CUBIC SIC FOR SEMICONDUCTOR-DEVICES [J].
NISHINO, S ;
POWELL, JA ;
WILL, HA .
APPLIED PHYSICS LETTERS, 1983, 42 (05) :460-462
[4]   Fabrication and testing of micromachined silicon carbide and nickel fuel atomizers for gas turbine engines [J].
Rajan, N ;
Mehregany, M ;
Zorman, CA ;
Stefanescu, S ;
Kicher, TP .
JOURNAL OF MICROELECTROMECHANICAL SYSTEMS, 1999, 8 (03) :251-257
[5]   CHARACTERIZATION OF N-TYPE BETA-SIC AS A PIEZORESISTOR [J].
SHOR, JS ;
GOLDSTEIN, D ;
KURTZ, AD .
IEEE TRANSACTIONS ON ELECTRON DEVICES, 1993, 40 (06) :1093-1099
[6]  
Sun Guosheng, 2004, Chinese Journal of Semiconductors, V25, P1205
[7]  
Sun Guosheng, 2003, Chinese Journal of Semiconductors, V24, P567
[8]   Advanced processing techniques for silicon carbide MEMS and NEMS [J].
Zorman, CA ;
Mehregany, M .
SILICON CARBIDE AND RELATED MATERIALS 2003, PTS 1 AND 2, 2004, 457-460 :1451-1456