Preparation of Fe/B powders by mechanical alloying

Steels with a high boron content are valuable as a neutron shield in waste containers and as control absorbers in nuclear reactors. The purpose of this study was to obtain by mechanical alloying an iron powder with 50% boron (by weight) and then powder-metallurgy materials. The elementary powders were mixed in a high-energy mill for 36h in an inert atmosphere. Samples were withdrawn at intervals, and the powder was characterized by differential thermal analysis, X-ray diffraction and electron microscopy. The Fe/B powders withdrawn at different intervals of milling were diluted with further additions of iron up to a final content of 10% boron. The mixtures were uniaxially compacted at 500 MPa; their green density was verified, and they were sintered in argon at 1150degreesC. Their physical properties (density and dimensional change) and bending strength were evaluated and microstructural studies and fracture tests were performed. (C) 2003 Elsevier Inc. All rights reserved.