Electrically conductive PANI-DBSA/Co-PAN composite fibers prepared by wet spinning

Conductive composite fibers of polyaniline doped with dodecylbenzene sulfonic acid (PANI-DBSA) and polyacrylonitrile containing methylacrylate (Co-PAN) were prepared via a conventional wet spinning process. The influences of PANI-DBSA content on the electrical conductivity, thermal stability and mechanical properties of the composite fibers were investigated. The fiber with 7 wt% PANI-DBSA showed its conductivity of an order of 10(-3) S/cm. The tensile strength of the fibers was in the range of 2.5-3.5 cN/dtex. The thermal stability of the composite fiber was superior to both pure Co-PAN and PANI-DBSA. It was observed through scanning electron microscope (SEM) and transmission electron microscope (TEM) that nanosized dot-like PANI-DBSA was well dispersed within Co-PAN matrix. (c) 2005 Elsevier B.V. All rights reserved.