ZrB2-SiC based composites for thermal protection by reaction sintering of ZrO2+B4C+Si

被引：35

作者：

Krishnarao, R. V. ^{[1
]}

Bhanuprasad, V. V. ^{[1
]}

Reddy, G. Madhusudhan ^{[1
]}

机构：

[1] Def Met Res Lab, Hyderabad 500058, Andhra Prades, India

来源：

JOURNAL OF ADVANCED CERAMICS | 2017年 / 6卷 / 04期

关键词：

ZrB2; SiC; reactive sintering; synthesis; composites; BORO/CARBOTHERMAL REDUCTION; MECHANICAL-PROPERTIES; SHOCK RESISTANCE; ZIRCONIUM; ZRO2; CERAMICS; TITANIUM; POWDERS; MICROSTRUCTURE; DIBORIDES;

D O I：

10.1007/s40145-017-0244-2

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Synthesis and sintering of ZrB2-SiC based composites have been carried out in a single-step pressureless reaction sintering (PLRS) of ZrO2, B4C, and Si. Y2O3 and Al2O3 were used as sintering additives. The effect of ratios of ZrO2/B4C, ZrO2/Si, and sintering additives (Y2O3 and Al2O3), was studied by sintering at different temperatures between 1500 and 1680 A degrees C in argon atmosphere. ZrB2, SiC, and YAG phases were identified in the sintered compacts. Density as high as 4.2 g/cm(3), micro hardness of 12.7 GPa, and flexural strength of 117.6 MPa were obtained for PLRS composites. Filler material was also prepared by PLRS for tungsten inert gas (TIG) welding of the ZrB2-SiC based composites. The shear strength of the weld was 63.5 MPa. The PLRS ZrB2-SiC composites exhibited: (i) resistance to oxidation and thermal shock upon exposure to plasma flame at 2700 A degrees C for 600 s, (ii) thermal protection for Cf-SiC composites upon exposure to oxy-propane flame at 2300 A degrees C for 600 s.

引用

页码：320 / 329

页数：10

共 38 条

[1] Fractographical characterization of hot pressed and pressureless sintered AlN-doped ZrB2-SiC composites [J].

Ahmadi, Zohre ;

Nayebi, Behzad ;

Asl, Mehdi Shahedi ;

Kakroudi, Mandi Ghassemi .

MATERIALS CHARACTERIZATION, 2015, 110 :77-85

[2] Modeling studies of the effect of twins on the X-ray diffraction patterns of boron carbide [J].

Anselmi-Tamburini, U ;

Ohyanagi, M ;

Munir, ZA .

CHEMISTRY OF MATERIALS, 2004, 16 (22) :4347-4351

[3] Synergetic effects of SiC and Csf in ZrB2-based ceramic composites. Part II: Grain growth [J].

Asl, Mehdi Shahedi ;

Kakroudi, Mandi Ghassemi ;

Farahbakhsh, Iman ;

Mazinani, Babak ;

Balak, Zohre .

CERAMICS INTERNATIONAL, 2016, 42 (16) :18612-18619

[4] Synergetic effects of SiC and Csf in ZrB2-based ceramic composites. Part I: Densification behavior [J].

Asl, Mehdi Shahedi ;

Golmohammadi, Fatemeh ;

Kakroudi, Mahdi Ghassemi ;

Shokouhimehr, Mohammadreza .

CERAMICS INTERNATIONAL, 2016, 42 (03) :4498-4506

[5] Optimization of effective parameters on thermal shock resistance of ZrB2-SiC-based composites prepared by SPS: Using Taguchi design [J].

Balak, Zohre ;

Azizieh, Mahdi ;

Kafashan, Hosein ;

Asl, Mehdi Shahedi ;

Ahmadi, Zohre .

MATERIALS CHEMISTRY AND PHYSICS, 2017, 196 :333-340

[6] Effect of different additives and open porosity on fracture toughness of ZrB2-SiC-based composites prepared by SPS [J].

Balak, Zohre ;

Asl, Mehdi Shahedi ;

Azizieh, Mandi ;

Kafashan, Hosein ;

Hayati, Raziye .

CERAMICS INTERNATIONAL, 2017, 43 (02) :2209-2220

[7] HYDROGENATION OF BORON MONOXIDE TO DIBORANE AND REACTIONS OF BORON AND BORON CARBIDE WITH TITANIUM AND ZIRCONIUM DIOXIDES [J].

BARTON, L ;

NICHOLLS, D .

JOURNAL OF INORGANIC & NUCLEAR CHEMISTRY, 1966, 28 (6-7) :1367-&

[8] Preparation and some properties of nanocrystalline ZrB2 powders [J].

Chen, LY ;

Gu, YL ;

Yang, ZH ;

Shi, L ;

Ma, JH ;

Qian, YT .

SCRIPTA MATERIALIA, 2004, 50 (07) :959-961

[9] 3D PRINTING Additive manufacturing of polymer-derived ceramics [J].

Eckel, Zak C. ;

Zhou, Chaoyin ;

Martin, John H. ;

Jacobsen, Alan J. ;

Carter, William B. ;

Schaedler, Tobias A. .

SCIENCE, 2016, 351 (6268) :58-62

[10] Refractory diborides of zirconium and hafnium [J].

Fahrenholtz, William G. ;

Hilmas, Gregory E. ;

Talmy, Inna G. ;

Zaykoski, James A. .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2007, 90 (05) :1347-1364

← 1 2 3 4 →