Sulfate resistance of alkali-activated slag/Portland cement mortar produced with lightweight pumice aggregate

被引：43

作者：

Dener, Murat ^{[1
,2
]}

Karatas, Mehmet ^{[1
]}

Mohabbi, Mehrzad ^{[2
]}

机构：

[1] Firat Univ, Civil Engn Dept, TR-23100 Elazig, Turkey

[2] Bingol Univ, Civil Engn Dept, TR-12000 Bingol, Turkey

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2021年 / 304卷

关键词：

Alkali-activated cement; Portland cement; Slag; Sulfate resistance; Lightweight aggregate; MECHANICAL-PROPERTIES; COMPRESSIVE STRENGTH; FLY-ASH; SLAG; GEOPOLYMERS; DURABILITY; ATTACK;

D O I：

10.1016/j.conbuildmat.2021.124671

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

In this study sulfate resistance of alkali-activated slag/Portland cement mortar produced with lightweight pumice aggregate was investigated. Slag was partly replaced with Portland cement at levels of 0 and 15% by weight. Alkali activator was prepared with a mix of sodium silicate (Na2SiO3) and sodium hydroxide (NaOH). The resistance to sulfate attack was investigated by exposing the mortar samples to 5% magnesium sulfate (MgSO4) and 5% sodium sulfate (Na2SO4) solutions for 1, 3 and 6 months, after which change in compressive strength and mass were determined. Microstructural deteriorations caused by sulfate attack were analyzed by FTIR. Excessive physical deterioration was observed in the mortars immersed in MgSO4 solution, but not in samples immersed in Na2SO4 solution. After all immersion periods in Na2SO4 solution, the compressive strength of both PC-free and 15% PC substituted mortars increased. This increase was higher in PC-free mortars. The compressive strength of mortars immersed in MgSO4 solution started to decrease from the 1st month of exposure.

引用

页数：8

共 50 条

[1] Sulfate resistance of alkali-activated slag and Portland cement based reactive powder concrete
Aydin, Serdar
Baradan, Bulent
JOURNAL OF BUILDING ENGINEERING, 2021, 43
[2] Fracture properties of alkali-activated slag and ordinary Portland cement concrete and mortar
Ding, Yao
Dai, Jian-Guo
Shi, Cai-Jun
CONSTRUCTION AND BUILDING MATERIALS, 2018, 165 : 310 - 320
[3] Resistance of Alkali-activated Slag Cement Against Sodium Sulfate
Allahverdi, A.
Hashemi, H.
Mahinroosta, M.
IRANIAN JOURNAL OF MATERIALS SCIENCE AND ENGINEERING, 2020, 17 (01) : 23 - 34
[4] Hydrated Portland cement as an admixture to alkali-activated slag cement
Rakhimova, Nailya R.
Rakhimov, Ravil Z.
ADVANCES IN CEMENT RESEARCH, 2015, 27 (02) : 107 - 117
[5] Alkali-silica reactivity of lightweight aggregates in alkali-activated slag cement and ordinary Portland cement systems
Yang, Shuqing
Poon, Chi Sun
Cui, Hongzhi
JOURNAL OF CLEANER PRODUCTION, 2023, 390
[6] Characterisation of ground hydrated Portland cement-based mortar as an additive to alkali-activated slag cement
Rakhimova, N. R.
Rakhimov, R. Z.
CEMENT & CONCRETE COMPOSITES, 2015, 57 : 55 - 63
[7] High temperature resistance of self compacting alkali activated slag/portland cement composite using lightweight aggregate
Dener, Murat
Karatas, Mehmet
Mohabbi, Mehrzad
CONSTRUCTION AND BUILDING MATERIALS, 2021, 290
[8] Alkali-activated Portland blast furnace slag cement mortars: Performance to alkali-aggregate reaction
Eugenia Angulo-Ramirez, Daniela
Mejia de Gutierrez, Ruby
Medeiros, Marcelo
CONSTRUCTION AND BUILDING MATERIALS, 2018, 179 : 49 - 56
[9] Investigating the resistance of alkali-activated slag mortar exposed to magnesium sulfate attack
Allahvedi, A.
Hashemi, H.
INTERNATIONAL JOURNAL OF CIVIL ENGINEERING, 2015, 13 (4A) : 379 - 387
[10] Individual and combined effects Of Portland cement-based hydrated mortar components on alkali-activated slag cement
Rakhimova, N. R.
Rakhimov, R. Z.
CONSTRUCTION AND BUILDING MATERIALS, 2014, 73 : 515 - 522

← 1 2 3 4 5 →