Effect of growth rate on microstructure parameters and microhardness in directionally solidified Ti-49Al alloy

被引：41

作者：

Fan, Jianglei ^{[1
]}

Li, Xinzhong ^{[1
]}

Su, Yanqing ^{[1
]}

Guo, Jingjie ^{[1
]}

Fu, Hengzhi ^{[1
]}

机构：

[1] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China

来源：

MATERIALS & DESIGN | 2012年 / 34卷

基金：

美国国家科学基金会;

关键词：

A; Intermetallics; C; Casting; E; Microhardness; TEMPERATURE-GRADIENT; PROCESSING PARAMETERS; SI ALLOYS; DEPENDENCY; SPACINGS;

D O I：

10.1016/j.matdes.2011.05.007

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Intermetallics Ti-49Al (at.%) alloy was directionally solidified with different growth rates (V = 5 mu m/s-30 mu m/s) at a constant temperature gradient (G = 12.1 K/mm) by using a Bridgman type directional solidification furnace. The primary dendritic spacing (lambda), interlamellar spacing (lambda(L)), and microhardness (HV) were measured. Effect of V on HV, lambda and lambda(L) was experimental investigated. The dependencies of lambda, lambda(L) and HV on the growth rate were determined by using linear regressing analysis. According to the result, the values of lambda and lambda(L) decrease with the increasing of V. and the values of HV increase with the increasing of V and with the decreasing of,. and L. The results were compared with previous similar experimental results for TiAl-based alloys. (C) 2011 Elsevier Ltd. All rights reserved.

引用

页码：552 / 558

页数：7

共 37 条

[31] Effect of Al2O3 particles on mechanical properties of directionally solidified intermetallic Ti-46Al-2W-0.5Si alloy [J].

Lapin, J ;

Ondrús, L ;

Bajana, O .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 360 (1-2) :85-95

[32] Directional solidification of intermetallic Ti-46Al-2W-0.5Si alloy in alumina moulds [J].

Lapin, J ;

Ondrús, L ;

Nazmy, M .

INTERMETALLICS, 2002, 10 (10) :1019-1031

[33] Lamellar orientation control of TiAl alloys under high temperature gradient with a Ti-43Al-Si seed [J].

Luo, Wenzhong ;

Shen, Jun ;

Min, Zhixian ;

Fu, Hengzhi .

JOURNAL OF CRYSTAL GROWTH, 2008, 310 (24) :5441-5446

[34] INTERDENDRITIC SPACING .2. A COMPARISON OF THEORY AND EXPERIMENT [J].

TRIVEDI, R .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (06) :977-982

[35] Review of alloy and process development of TiAl alloys [J].

Wu, Xinhua .

INTERMETALLICS, 2006, 14 (10-11) :1114-1122

[36] Directional solidification of TiAl-base alloys [J].

Yamaguchi, M ;

Johnson, DR ;

Lee, HN ;

Inui, H .

INTERMETALLICS, 2000, 8 (5-6) :511-517

[37] Directional solidification of TiAl-Re-Si alloys with aligned γ/α2 lamellar microstructures [J].

Yamanaka, T ;

Johnson, DR ;

Inui, H ;

Yamaguchi, M .

INTERMETALLICS, 1999, 7 (07) :779-784

← 1 2 3 4 →